EFEITO DO MOLIBDÊNIO E NIÓBIO NA MICROESTRUTURA, RESISTÊNCIA AO IMPACTO E À CORROSÃO DE AÇOS MICROLIGADOS

MOLYBDENUM AND NIOBIUM EFFECT ON MICROSTRUCTURE, IMPACT AND CORROSION RESISTANCE OF MICROALLOYED STEELS

DOI

10.5151/2594-5327-33267

Downloads

Baixar Artigo 249 Downloads

Resumo

Os aços de alta resistência e baixa liga são largamente utilizados na fabricação de tubulações de petróleo, pois apresentam propriedades mecânicas adequadas de acordo com a norma API. O principal processo de fabricação desses aços é a laminação controlada, no entanto, para peças com geometria complexa, o forjamento é o preferido. Nesse caso, são necessários tratamentos térmicos de têmpera e revenimento para o alcance das propriedades. Além das solicitações mecânicas e da alta pressão que as tubulações devem suportar, esses materiais devem ainda resistir à corrosão causada pela água do mar. Dentro deste contexto, o objetivo desse trabalho é avaliar a microestrutura, resistência ao impacto e à corrosão de dois aços microligados com diferentes teores de nióbio e molibdênio. Inicialmente dois lingotes de aços foram forjados e posteriormente submetidos aos tratamentos de têmpera e revenimento. A partir da curva de revenimento, uma temperatura média da faixa do endurecimento secundário, segundo resultados da literatura, foi selecionada para a realização dos ensaios de impacto e polarização potenciodinâmica. Os resultados mostram que o aço com maior teor de nióbio apresenta maior resistência ao impacto e à corrosão, enquanto o aço com maior teor de molibdênio apresenta maior dureza.

 

High strength and low alloy steels are widely used in petroleum pipes manufacturing, because presents mechanical properties according to API standard. The main manufacturing process for these steels is the controlled rolling, however, for complex geometry parts, forging is preferred. In this case, quenching and tempering heat treatments are necessary to reach the desired properties. Besides mechanical and high-pressure requests which the pipes must support, these materials must still resist seawater corrosion. In this context, the current work goal is to evaluate the microstructure, impact and corrosion resistance of two microalloyed steels with different niobium and molybdenum content. Initially two steels ingots were forged and subsequently subjected to quenching followed by tempering treatments. From the tempering curve, an average temperature of secondary hardening range, according to literature results, was selected to impact and potentiodynamic polarization tests. The results show that the steel with highest niobium content delivers higher impact and corrosion resistance, while the steel with higher molybdenum content delivers higher hardness.

Palavras-chave

Aço microligado; Ferrita acicular; Bainita; Corrosão.

Microalloyed steel; Acicular ferrite; Bainite; Corrosion.

Como citar

Mazini, Jaqueline Polezi; Filho, André Itman; Ávila, Breno Mendes Rabelo; Junior, Dirceu da Silva; Oliveira, Pedro Gabriel Bonella de. EFEITO DO MOLIBDÊNIO E NIÓBIO NA MICROESTRUTURA, RESISTÊNCIA AO IMPACTO E À CORROSÃO DE AÇOS MICROLIGADOS , p. 683-691. In: 74º Congresso Anual da ABM, São Paulo, 2019.