EFEITO DOS PARÂMETROS DE SOLDAGEM DO PROCESSO PTA NAS CARACTERÍSTICAS GEOMÉTRICAS E NO TEOR DE FERRITA DO METAL DE SOLDA NA DEPOSIÇÃO DE AÇO INOXIDÁVEL SUPERDUPLEX

EFFECT OF WELDING PARAMETERS OF PTA PROCESS ON GEOMETRICAL FEATURES AN WELD METAL FERRITE CONTENT IN DEPOSITION OF SUPERDUPLEX STAINLESS STEEL

DOI

10.5151/2594-5327-22937

Downloads

Baixar Artigo 249 Downloads

Resumo

O objetivo deste trabalho é avaliar as características geométricas e o teor de ferrita no metal de solda em soldagens de revestimentos de dutos de aço C-Mn, com deposição de AISD UNS S32760 pelo processo PTA. Empregou-se o Método Estatístico Taguchi para planejamento experimental e avaliação das variáveis do processo: vazão de gás plasma (1 l/min, 3 l/min e 5 l/min.); vazão de gás de proteção (10 l/min, 15 l/min e 20 l/min); tipo de gás de proteção (Ar, Ar + 2,5%N2 e Ar + 25%He) e DBP (8 mm, 12 mm e 16 mm). Foram realizadas soldagens de cordões simples e foi feita a preparação de amostras por metalografia, quantificação do teor de ferrita e avaliação das características geométricas nas seções transversais das amostras cortadas. A condição de soldagem empregando DBP de 16 mm, Ar + 25%He como gás de proteção (15 l/min) e vazão gás plasma (3 l/min) resultou em melhores características para revestimentos. Os cordões de solda apresentaram reforços acima de 3 mm, maior largura, menor ângulo de molhamento, baixo nível de diluição e teor de ferrita satisfatório.

 

The aim this work is to evaluate the influence the geometric characteristics and ferrite content in the weld metal in weld overlay on C-Mn steel pipes with SDSS UNS S32760 deposition by PTA process. Taguchi method had been used for experimental arrangement and evaluation of process variables: plasma gas flow rate (1 l/min, 3 l/min and 5 l/min), shielding gas flow rate (10 l/min, 15 l/min and 20 l/min), kind of shielding gas (Ar, Ar + 2,5%N2 and Ar + 25%He) and torch work distance (8 mm, 12 mm and 16 mm). Welding has been performed with only one bead deposited. Later, it had carried geometry analysis and quantification of ferrite content in the weld metal. In relation to the reinforcement, width, wetting, dilution and content ferrite, the SDSS powder was successfully deposited using the PTA welding process: torch work distance – 16 mm; shielding gas – Ar + 25%He; shielding gas flow rate – 15 l/min and plasma gas flow rate – 3 l/min.

Palavras-chave

PTA; Revestimento; Superduplex; Geometria.

PTA; Weld overlay; Superduplex; Geometry.

Como citar

Nunes, Everton Barbosa; Barreto, Alexandre Sousa; Santos, Davi Marinho dos; Miranda, Edvan Cordeiro de; Motta, Marcelo Ferreira. EFEITO DOS PARÂMETROS DE SOLDAGEM DO PROCESSO PTA NAS CARACTERÍSTICAS GEOMÉTRICAS E NO TEOR DE FERRITA DO METAL DE SOLDA NA DEPOSIÇÃO DE AÇO INOXIDÁVEL SUPERDUPLEX , p. 612-623. In: 68º Congresso da ABM, São Paulo, 2013.