O LATãO é O NOME DADO àS LIGAS DE COBRE COM ADIçãO DE ZINCO (ZN), AMPLAMENTE UTILIZADAS NA INDúSTRIA DEVIDO à SUA EXCELENTE COMBINAçãO DE PROPRIEDADES FíSICAS E MECâNICAS. ESTE ESTUDO TEM COMO OBJETIVO AVALIAR A INFLUêNCIA DE DIFERENTES TEMPERATURAS DE RECOZIMENTO NA MICROESTRUTURA E NO COMPORTAMENTO MECâNICO DO LATãO C36000, COMPARANDO OS RESULTADOS COM AS CARACTERíSTICAS DO MESMO MATERIAL NA CONDIçãO DE COMO RECEBIDO (COMO EXTRUDADO). AS AMOSTRAS FORAM TRATADOS TERMICAMENTE EM TEMPERATURAS VARIANDO DE 250°C A 850°C POR 1 HORA EM CADA NíVEL, SEGUIDO DE RESFRIAMENTO IMEDIATO EM áGUA. EM SEGUIDA, TANTO A AMOSTRA COMO RECEBIDA QUANTO AS TRATADAS TERMICAMENTE FORAM CARACTERIZADAS UTILIZANDO MICROSCOPIA óPTICA, MICROSCOPIA ELETRôNICA DE VARREDURA, DIFRAçãO DE RAIOS-X, DUREZA E TESTES DE COMPRESSãO. AS CARACTERIZAçõES MICROESTRUTURAIS REVELAM QUE TANTO A AMOSTRA COMO RECEBIDA QUANTO AS TRATADAS TERMICAMENTE EXIBEM UMA MICROESTRUTURA BIFáSICA (α + β), COM UMA MUDANçA DRáSTICA NAS FRAçõES DE FASE OBSERVADAS APENAS PARA TEMPERATURAS ACIMA DE 400°C. DO PONTO DE VISTA DAS PROPRIEDADES MECâNICAS, HOUVE UM AUMENTO NA RESISTêNCIA MECâNICA COM O AUMENTO DA TEMPERATURA ATé 550°C. NO ENTANTO, HOUVE UMA DIMINUIçãO NA RESISTêNCIA MECâNICA E UM AUMENTO NA DUREZA EM TEMPERATURAS ACIMA DE 550°C DEVIDO AO AUMENTO NA FRAçãO DE VOLUME E NO TAMANHO DE GRãO DA FASE β, QUE é MAIS DURA E MENOS DúCTIL DO QUE A FASE α.
BRASS IS THE NAME GIVEN TO COPPER ALLOYS WITH THE ADDITION OF ZINC (ZN), WHICH ARE WIDELY USED IN INDUSTRY DUE TO THEIR EXCELLENT COMBINATION OF PHYSICAL AND MECHANICAL PROPERTIES. THIS STUDY AIMS TO EVALUATE THE INFLUENCE OF DIFFERENT ANNEALING TEMPERATURES ON THE MICROSTRUCTURE AND MECHANICAL BEHAVIOUR OF C36000 BRASS AND COMPARED THE RESULTS WITH THE CHARACTERISTICS OF THE SAME MATERIAL IN THE AS-RECEIVED CONDITION (AS EXTRUDED CONDITION). THE SPECIMENS WERE HEAT TREATED AT TEMPERATURES RANGING FROM 250°C TO 850°C FOR 1 HOUR AT EACH LEVEL, FOLLOWED BY IMMEDIATE QUENCHING IN WATER. AFTERWARD, BOTH THE AS-RECEIVED SPECIMENS AND THE HEAT TREATED SPECIMENS WERE CHARACTERIZED USING OPTICAL MICROSCOPY, SCANNING ELECTRON MICROSCOPY, X-RAY DIFFRACTION, HARDNESS, AND COMPRESSION TESTS. THE MICROSTRUCTURAL CHARACTERIZATIONS REVEAL THAT BOTH THE AS-RECEIVED SPECIMEN AND THE HEAT TREATED SPECIMENS EXHIBIT A BIPHASIC MICROSTRUCTURE (
Palavras-chave
Ligas de latão; Tratamento térmico; Caracterização microestrutural; Propriedades mecânicas
Brass alloys; Heat treatment; Microstructure Characterization; Mechanical Properties
Como citar
ONISHI, MICHELLE MIDORI;
DANNINGER, LEONARDO RODRIGUES;
RIOS, CARLOS TRIVEÑO.
EFEITOS DA TEMPERATURA DE TRATAMENTO TÉRMICO NA MICROESTRUTURA E EM ALGUMAS PROPRIEDADES MECÂNICAS DO LATÃO C36000
,
p. 211-222.
In: 77º Congresso Anual da ABM - Internacional,
São Paulo, Brasil,
2024.
ISSN: 2594-5327
, DOI 10.5151/2594-5327-40484