ESTÁGIO INICIAL DA SINTERIZAÇÃO CONVENCIONAL DE LIGAS TI-NB A PARTIR DE PÓS ELEMENTARES

CONVENTIONAL SINTERING INITIAL STAGE OF TI-NB ALLOYS FROM ELEMENTARY POWDERS

Autoria

Reznik, Bernard; Magalhães, Gustavo Gullit Leal; Lima, Lucas Vinicius Silveira de; Silva, Matheus Domingos Ferreira da; Pereira, Antônio de Souza Gomes; Tavares, Pedro Henrique Monteiro; Melo, Edilainea Alves Oliveira; Sénéchal, Naiara Vieira Le; Teixeira, Rodolfo da Silva; Paula, Andersan dos Santos

DOI

10.5151/2594-5327-34287

Downloads

Baixar Artigo 9 Downloads

Resumo

O PRESENTE TRABALHO AVALIOU OS ESTÁGIOS INICIAIS DA SINTERIZAÇÃO CONVENCIONAL, SOB ATMOSFERA OXIDANTE, DE LIGAS BASEADAS NO SISTEMA TI-NB COM 8,34 E 25,57%AT.NB, COM USO DE PÓS ELEMENTARES DE TI E NB ORIUNDOS DO PROCESSO DE HIDRETAÇÃO-DEHIDRETADO (HDH), QUE ENVOLVE UM PROCESSO E MATÉRIAS-PRIMAS DE MENOR CUSTO PARA PRODUÇÃO DESTAS LIGAS. A AVALIAÇÃO DAS DENSIDADES TEÓRICA E EXPERIMENTAL (PRINCÍPIO DE ARQUIMEDES) RESSALTARAM CARACTERÍSTICAS IMPORTANTES SOBRE A MISTURA INICIAL DE PÓS DE TI E NB COM DISTINTAS GRANULOMETRIAS, CORROBORANDO COM OS RESULTADOS OBTIDOS A PARTIR DAS ANÁLISES DE MICROSCOPIA ELETRÔNICA DE VARREDURA E DIFRAÇÃO DE RAIOS X – PELA FORMAÇÃO INICIAL DO INTERMETÁLICO TINB ENTRE AS PARTÍCULAS DE TI E NB EM CONJUNTO COM ALGUNS ÓXIDOS E SUBÓXIDOS.

 

THE PRESENT STUDY EVALUATED THE INITIAL STAGES OF CONVENTIONAL SINTERING ALLOYS, OXIDIZING ATMOSPHERE, BASED ON TI-NB SYSTEM WITH 8.34 AND 25.57%AT.NB, USING TI AND NB ELEMENTARY POWDERS FROM THE HYDRATION-DEHYDRATION (HDH) PROCESS, WHICH INVOLVES A LOWER COST PROCESS AND RAW MATERIALS FOR THE PRODUCTION OF THESE ALLOYS. THE EVALUATION OF THEORETICAL AND EXPERIMENTAL DENSITIES (ARCHIMEDES PRINCIPLE) HIGHLIGHTED IMPORTANT CHARACTERISTICS ABOUT THE INITIAL MIXTURE OF TI AND NB POWDERS WITH DIFFERENT PARTICLE SIZES, CORROBORATING WITH THE RESULTS OBTAINED FROM THE SCANNING ELECTRON MICROSCOPY AND X-RAY DIFFRACTION ANALYZES - BY THE INITIAL FORMATION OF THE TINB INTERMETALLIC BETWEEN THE TI AND NB PARTICLES ASSOCIATED WITH SOME OXIDES AND SUBOXIDES.

Palavras-chave

Liga com Memória de Forma; Ti-Nb; Sinterização Convencional

Shape Memory Alloys; Ti-Nb; Conventional Sintering