Título

ESTUDO COMPARATIVO DE CORROSÃO PREFERENCIAL EM SOLDAS DE LINHAS DE DECAPAGEM ÁCIDA DE UMA USINA SIDERÚRGICA

COMPARATIVE STUDY OF PREFERENTIAL CORROSION IN WELDS OF ACID PICKLING LINE IN STEEL MILLS

Autoria

Fernandes, Vinicius Santiago

DOI

10.5151/2594-5327-34891

Downloads

Baixar Artigo 16 Downloads

Resumo

AVALIOU-SE À CORROSÃO PREFERENCIAL DE JUNTAS SOLDADAS DE AÇOS BAIXO CARBONO EM AMBIENTES QUE SIMULAM LINHAS DE DECAPAGEM ÁCIDA, COM INTUITO DE ENTENDER E PREVENIR POSSÍVEIS FALHAS DE ARREBENTAMENTOS DE SOLDAS DENTRO DE TANQUES DE DECAPAGEM EM UM PROCESSO SIDERÚRGICO. A FRAGILIZAÇÃO NA REGIÃO DA SOLDA E OS SEUS EFEITOS NAS PROPRIEDADES DAS JUNTAS FORAM AVALIADOS POR MEIO DE ENSAIOS DE CORROSÃO E METALOGRÁFICOS. OBSERVOU-SE A CORROSÃO PREFERENCIAL NA REGIÃO DA SOLDA NOS PROCESSOS DE SOLDAGEM A LASER E CENTELHAMENTO, PELA PRESENÇA DE DESCONTINUIDADES SUPERFICIAIS, TENSÕES RESIDUAIS E MICROESTRUTURA SUSCEPTÍVEL, ESTA FRAGILIZAÇÃO SÓ OCORREU QUANDO AS SOLDAS FICARAM IMERSAS EM UM AMBIENTE ÁCIDO UM TEMPO SUPERIOR AO PREVISTO NO PROCESSAMENTO DO MATERIAL. CONCLUIU-SE QUE A PARTIR DE UM TEMPO ELEVADO DE PERMANÊNCIA DE UMA SOLDA EM UM AMBIENTE ÁCIDO COM TEMPERATURA EM TORNO DE 60°C, A CORROSÃO PREFERENCIAL TENDE A OCORRER NA REGIÃO DA SOLDA.

 

THE PREFERENTIAL CORROSION OF WELDED JOINTS OF LOW CARBON STEELS WAS EVALUATED IN ENVIRONMENTS THAT SIMULATE ACID PICKLING SECTION, IN ORDER TO UNDERSTAND AND PREVENT POSSIBLE WELD BREAKS INSIDE PICKLING TANKS IN A STEELMAKING PROCESS. EMBRITTLEMENT IN THE WELD REGION AND ITS EFFECTS ON JOINT PROPERTIES WERE EVALUATED BY CORROSION AND METALLOGRAPHIC TESTS. PREFERENTIAL CORROSION WAS OBSERVED IN THE WELD REGION IN BOTH, LASER AND FLASH BUTT WELDING DUE TO THE PRESENCE OF SURFACE DISCONTINUITIES, RESIDUAL STRESSES AND SUSCEPTIBLE MICROSTRUCTURE, THIS EMBRITTLEMENT ONLY OCCURRED WHEN THE WELDS WERE IMMERSED IN AN ACIDIC ENVIRONMENT FOR A LONGER TIME THAN PREDICTED IN THE MATERIAL PROCESSING. IT WAS CONCLUDED THAT FROM A LONG TIME OF PERMANENCE OF A WELD IN AN ACID ENVIRONMENT WITH TEMPERATURE AROUND 60°C, THE PREFERENTIAL CORROSION TENDS TO OCCUR IN THE REGION OF THE WELD.

Palavras-chave

Soldagem; Corrosão; Fragilização; Decapagem

Welding; Corrosion; Embrittlement; Pickling