ESTUDO DA INTERAÇÃO ENTRE DENSIDADE DE LINHAS DE CAMPO E PRESENÇA DE FASE SIGMA DE UM AÇO INOXIDÁVEL DUPLEX ATRAVÉS DE DO ESTUDO DE MEDIDAS DE TENSÃO HALL

STUDY OF THE INTERACTION BETWEEN DENSITY OF LINES AND FIELD PRESENCE OF SIGMA PHASE OF A DUPLEX STAINLESS STEEL THROUGH THE STUDY HALL VOLTAGE MEASUREMENT

DOI

10.5151/1516-392X-25175

Downloads

Baixar Artigo 188 Downloads

Resumo

Aços inoxidáveis duplex apresentam boas propriedades mecânicas e de resistência à corrosão, mas quando são colocados para trabalhar em altas temperaturas como no processo de soldagem e de tratamento térmico ocorre o surgimento de fases que comprometem as suas propriedades. Dentre elas, a fase sigma (s) é a que apresenta um maior efeito de fragilização por ser rica em cromo e empobrecer a matriz desse elemento, bem como por apresentar dureza em torno de 1000HV. No presente trabalho, uma metodologia não destrutiva, baseada na interação entre densidade de linhas de campo e um aço inoxidável duplex, é apresentada para o acompanhamento da formação da fase s na temperatura de 800°C em um aço envelhecido por até 2 horas. Diferentes intensidades de campo foram geradas por um eletroímã e o fluxo de linhas de campo foi aplicado no material de estudo. A densidade de linhas de campo resultante foi medida por um sensor de efeito Hall. Os resultados foram correlacionados com resultados de microscopia eletrônica de varredura (MEV), dureza e difração de raios-X (DRX) e mostraram que os valores de tensão hall reduziram à medida que a fração volumétrica da fase s aumentou. A formação dessa fase não magnética influenciou no sinal obtido pelo sensor Hall. Existiu uma correlação entre a densidade de linhas de campo resultante e a presença da fase fragilizante, apontando para uma metodologia capaz de acompanhar a formação dessa fase.

 

Duplex stainless steels have good mechanical and corrosion resistance properties, but when submitted to high temperatures as in welding and heat treatment process occurs the formation of phases that compromise their properties. Among then, the sigma phase (s) is what causes the most embrittlement effect to be rich in chromium and reduce the matrix of this element, as well as presenting hardness around 1000HV. In this study, a non-destructive methodology, based on the interaction between magnetic flux density and a duplex stainless steel it is parsed for monitoring the formation of s phase at a temperature of 800°C, for samples aged for times up to 2 hours. Different magnetic field were generated and applied into the study material. The magnetic flux density was measured by a Hall effect sensor. The results were correlated with the ones of scanning electron microscopy (SEM), hardness and X-ray diffraction (XRD). The results showed that the Hall voltage measurements were able to follow the formation of s phase. The formation of this non-magnetic phase influenced the signal obtained by the Hall sensor, reducing the voltage. There was a correlation between magnetic flux density and the phase embrittlement, pointing to a methodology able to follow the formation of this phase.

Palavras-chave

Fase sigma; Ensaio não destrutivo; Densidade de linhas de campo

Sigma phase; Nondestructive test; Magnetic flux density

Como citar

Edgard de Macedo Silva; Ana Lucia Silva Souza Andrade; Bruno Ribeiro de Araújo; Josinaldo Pereira Leite; Walter de Macêdo Lins Fialho; João Pereira Leiter. ESTUDO DA INTERAÇÃO ENTRE DENSIDADE DE LINHAS DE CAMPO E PRESENÇA DE FASE SIGMA DE UM AÇO INOXIDÁVEL DUPLEX ATRAVÉS DE DO ESTUDO DE MEDIDAS DE TENSÃO HALL , p. 9223-9230. In: 69° Congresso Anual da ABM - Internacional, São Paulo - Brasil, 2014.