EVOLUÇÃO COMPARATIVA DA MICROESTRUTURA E TEXTURA EM CHAPAS DE LIGA DE ALUMÍNIO AA1050 PRODUZIDO PELO PROCESSO DC E CC

COMPARATIVE MICROSTRUCTURE AND TEXTURE EVOLUTION IN THE AA1050 ALUMINUM ALLOY SHEETS PRODUCED BY DC AND CC METHODS

Autoria

Otomar, Heber Pires; Plaut, Ronald Lesley

10.5151/2594-5297-17615

Downloads

Baixar Artigo 109 Downloads

Resumo

Este estudo visa à avaliação, em escala industrial, do efeito entre os processos de fabricação de fundição contínua (CC) e vazamento Direto (DC) sobre a liga de alumínio AA1050 laminada e recozida. Caracterização da evolução da microestrutura e textura do vazamento até a condição final após a conformação foi realizado. Foram realizados ensaios de estampagem para identificar qual processo apresenta desempenho melhor. Microestruturas diferentes foram obtidas para os processos de estudo: o material de DC foi mais homogêneo, tanto em termos de distribuição de intermetálicos e tamanho de grãos. As propriedades mecânicas do material CC foram superiores em relação ao material de DC. O material do processo CC com homogeneização apresentou o melhor desempenho para a Curva Limite de Conformação (CLC).

This study aims at the evaluation, in an industrial scale, of the effect between the direct chill (DC) and continuous casting (CC) fabrication processes of AA1050 rolled and annealed sheets. Characterization of their microstructure and texture evolution from the as-cast condition up to the end condition of a deep-drawn cup has been carried out. Stamping tests have been performed to identify which process presents best stamping performance. Different microstructures have been obtained for the studied processes: the DC material was more homogeneous, both in terms of intemetallic distribution and grain size. The mechanical properties of the CC material, were slightly higher than those for the DC material. Forming limit diagram (FLD) the homogenized CC material presented the best results.

Palavras-chave

Ligas de alumínio; Conformação mecânica.

Aluminum alloys, Mechanical working; Heat treatment.