INCORPORAÇÃO DE CINZA LEVE DE CALDEIRA EM CERÂMICA VERMELHA

INCORPORATION A LIGHT ASH BOILER IN RED CERAMIC

Autoria

Delaqua, Geovana Carla Girondi; Coelho, Gabriel Neves Araújo; Pires, Diego Alexsander Moreira; Marvila, Markssuel Teixeira; Azevedo, Afonso Rangel Garcez de; Souza, Djalma; Pereira, Elaine Cristina; Jr, Fernando Vernilli; Vieira, Carlos Maurício Fontes

DOI

10.5151/2594-5327-34924

Downloads

Baixar Artigo 29 Downloads

Resumo

A INDÚSTRIA DE PAPEL E CELULOSE TRADICIONALMENTE DEPARAM-SE COM PROBLEMAS DE ORDEM AMBIENTAL DEVIDO À GRANDE QUANTIDADE DE RESÍDUOS GERADOS, DOS QUAIS SE DESTACAM AS CINZAS DE CALDEIRA DE BIOMASSA E OS EFLUENTES LÍQUIDOS. A CINZA SURGE COMO UM VERDADEIRO DESAFIO, POIS APRESENTA CAPACIDADE EROSIVA E NÃO SE QUEIMA, REQUERENDO UM SISTEMA PRÓPRIO PARA RETIRADA. DESTA FORMA, ESTE TRABALHO TEM COMO OBJETIVO AVALIAR A VIABILIDADE DA INCORPORAÇÃO DA CINZA LEVE DE CALDEIRA EM CERÂMICA VERMELHA. AS MATÉRIAS-PRIMAS FORAM INICIALMENTE SUBMETIDAS A ENSAIOS DE CARACTERIZAÇÃO, E PREPARADAS COMPOSIÇÕES COM DIFERENTES PORCENTAGENS DE 0; 2,5; 5; 10 E 20% EM MASSA DE CINZA LEVE NA MASSA CERÂMICA. OS CORPOS DE PROVA FORAM CONFORMADOS POR PRENSAGEM UNIAXIAL E QUEIMADOS EM TEMPERATURAS DE 600 A 1050ºC, E ENTÃO SUBMETIDOS A ENSAIOS TECNOLÓGICOS, TAIS COMO: ABSORÇÃO DE ÁGUA E RESISTÊNCIA À COMPRESSÃO. OS RESULTADOS EXPERIMENTAIS INDICARAM QUE O RESÍDUO DE CINZA LEVE DE EUCALYPTUS GRANDIS INFLUENCIOU POSITIVAMENTE AS PROPRIEDADES TECNOLÓGICAS DAS PEÇAS DE CERÂMICA VERMELHA. OS RESULTADOS TAMBÉM MOSTRARAM QUE ENTRE 5 E 10 % EM PESO DE RESÍDUO DE CINZA COMO SUBSTITUTO PARCIAL DE ARGILA PLÁSTICA PERMITE A OBTENÇÃO DE PRODUTOS DE CERÂMICA VERMELHA DE ÓTIMA QUALIDADE TÉCNICA

 

THE PULP AND PAPER INDUSTRY TRADITIONALLY BREAKS DOWN ENVIRONMENTAL PROBLEMS DUE TO THE LARGE AMOUNT OF WASTE GENERATED, OF WHICH STAND OUT AS BIOMASS BOILER ASH AND WASTEWATER. AN INCREASE IN ASH AS A REAL CHALLENGE, AS IT HAS EROSIVE CAPACITY AND DOES NOT BURN, REQUIRING ITS OWN SYSTEM FOR REMOVAL. THIS WORK AIMS TO EVALUATE THE FEASIBILITY OF INCORPORATING A RED CERAMIC ASH BOILER. THE RAW MATERIALS WERE SUBJECTED TO CHARACTERIZATION TESTS, AND COMPOSITIONS WERE PREPARED WITH DIFFERENT PERCENTAGES OF 0; 2.5; 5; 10 AND 20% BY WEIGHT OF LIGHT ASH IN THE CERAMIC MASS. THE CERAMIC SPECIMENS WERE PRESSED-SHAPED AND FIRED AT 600 TO 1050ºC AND SUBSEQUENTLY THE TESTS WERE TECHNOLOGICALLY TESTED, SUCH AS: LINEAR SHRINKAGE, WATER ABSORPTION AND COMPRESSIVE STRENGTH. EXPERIMENTAL RESULTS INDICATE THAT THE EUCALYPTUS LIGHT ASH WASTE AS POSITIVELY INFLUENCED THE TECHNOLOGICAL PROPERTIES OF THE RED CERAMIC PIECES. THE RESULTS ALSO SHOW THAT BETWEEN 5 AND 10% IN ASH WASTE AS A PARTIAL SUBSTITUTE OF PLASTIC CLAY ALLOWS THE USE OF RED CERAMIC PRODUCTS OF EXCELLENT TECHNICAL QUALITY

Palavras-chave

Cinza leve; Resíduo; Eucalyptus grandis; Cerâmica vermelha

Light ash; Waste; Eucalyptus grandis; Red ceramic