Título

INCORPORAÇÃO DE CINZAS CERÂMICAS EM ARGAMASSAS DE ASSENTAMENTO

INCORPORATION OF CERAMIC ASHES IN SETTING MORTARS

Autoria

Cruz, Ariana Silva Azeredo; Marvila, Markssuel Teixeira; Azevedo, Afonso Rangel Garcez de; Júnior, José Alexandre Tostes Linhares; Cruz, Lucas Reis; Delaqua, Geovana Carla Girondi; Monteiro, Sergio Neves; Cecchin, Daiane; Alexandre, Jonas; Vieira, Carlos Maurício Fontes

DOI

10.5151/2594-5327-34066

Downloads

Baixar Artigo 10 Downloads

Resumo

A INDÚSTRIA CERAMISTA É RESPONSÁVEL PELO DESCARTE INADEQUADO DE MILHÕES DE TONELADAS DE RESÍDUOS, PROVENIENTES DE FALHAS NO SEU PROCESSO PRODUTIVO, NO MEIO AMBIENTE. A FIM DE BUSCAR UMA ALTERNATIVA DE USO DESTE MATERIAL, VISANDO DIMINUIR O IMPACTO AMBIENTAL DA PRODUÇÃO CERÂMICA, ESTE TRABALHO TEVE COMO OBJETIVO AVALIAR A VIABILIDADE TÉCNICA DO USO DE CINZAS RESIDUAIS DE INDUSTRIAS CERÂMICAS EM ARGAMASSAS, COMO SUBSTITUIÇÃO PARCIAL DO CIMENTO PORTLAND. PARA ISTO, FORAM CONFECCIONADAS TRÊS ARGAMASSAS NO TRAÇO 1:1:6 (CIMENTO: CAL HIDRATADA: AREIA), A PRIMEIRA USADA COMO REFERÊNCIA, SEM PRESENÇA DE RESÍDUO, E POR FIM, ARGAMASSAS UTILIZANDO 5 E 10% DE CINZAS RESIDUAIS DA PRODUÇÃO CERÂMICA, RESPECTIVAMENTE. AS ARGAMASSAS FORAM SUBMETIDAS AOS ENSAIOS DE ÍNDICE DE CONSISTÊNCIA, RETENÇÃO DE ÁGUA E DENSIDADE DE MASSA E TEOR DE AR INCORPORADO, PELOS QUAIS FOI CONSTATADO QUE A PRESENÇA DO RESÍDUO CONTRIBUI PARA O AUMENTO DA RETENÇÃO DE ÁGUA DA ARGAMASSA, BEM COMO PARA O AUMENTO DA DENSIDADE E O DECRÉSCIMO DO TEOR DE AR INCORPORADO A MESMA. ADEMAIS, NÃO REPRESENTA DANOS A CONSISTÊNCIA, APESAR DE NÃO PROMOVER MELHORA SIGNIFICATIVA DESTA CARACTERÍSTICA. FOI POSSÍVEL, PORTANTO, CONCLUIR QUE O USO DE CINZAS RESIDUAIS DA PRODUÇÃO CERÂMICA COMO SUBSTITUIÇÃO PARCIAL AO CIMENTO PORTLAND EM ARGAMASSAS NÃO TRAZ DANOS ÀS PROPRIEDADES FÍSICAS DA ARGAMASSA NO ESTADO FRESCO.

 

THE CERAMIST INDUSTRY IS RESPONSIBLE FOR THE INAPPROPRIATE DISPOSAL OF MILLIONS OF TONS OF WASTE, RESULTING FROM FAILURES IN ITS PRODUCTION PROCESS, IN THE ENVIRONMENT. IN ORDER TO SEEK AN ALTERNATIVE USE OF THIS MATERIAL, AIMING TO REDUCE THE ENVIRONMENTAL IMPACT OF CERAMIC PRODUCTION, THIS WORK AIMED TO EVALUATE THE TECHNICAL FEASIBILITY OF USING RESIDUAL ASHES FROM CERAMIC INDUSTRIES IN MORTARS, AS A PARTIAL REPLACEMENT OF PORTLAND CEMENT. FOR THIS, THREE MORTARS WERE MADE IN THE MIX 1: 1: 6 (CEMENT: HYDRATED LIME: SAND), THE FIRST USED AS A REFERENCE, WITHOUT THE PRESENCE OF RESIDUE, AND FINALLY, MORTARS USING 5 AND 10% OF RESIDUAL ASH FROM CERAMIC PRODUCTION , RESPECTIVELY. THE MORTARS WERE SUBJECTED TO THE TESTS OF CONSISTENCY INDEX, WATER RETENTION AND MASS DENSITY AND INCORPORATED AIR CONTENT, BY WHICH IT WAS FOUND THAT THE PRESENCE OF THE RESIDUE CONTRIBUTES TO THE INCREASE IN THE WATER RETENTION OF THE MORTAR, AS WELL AS TO THE INCREASE OF DENSITY AND THE DECREASE IN THE AIR CONTENT INCORPORATED INTO IT. FURTHERMORE, IT DOES NOT REPRESENT DAMAGE TO CONSISTENCY, ALTHOUGH IT DOES NOT PROMOTE SIGNIFICANT IMPROVEMENT OF THIS CHARACTERISTIC. IT WAS THEREFORE POSSIBLE TO CONCLUDE THAT THE USE OF RESIDUAL ASH FROM CERAMIC PRODUCTION AS A PARTIAL REPLACEMENT FOR PORTLAND CEMENT IN MORTARS DOES NOT HARM THE PHYSICAL PROPERTIES OF THE MORTAR IN ITS FRESH STATE.

Palavras-chave

Resíduo; Cinzas; Argamassa

Residue; Ashes; Mortar