INCORPORAÇÃO DE RESÍDUO DE VIDRO PLANO EM CERÂMICA VERMELHA

INCORPORATION OF FLAT GLASS WASTE IN RED CERAMICS

Autoria

Delaqua, Geovana Carla Girondi; Magalhães, Juan Peixoto Barroco; Marvila, Markssuel Teixeira; Vieira, Carlos Maurício Fontes

DOI

10.5151/2594-5327-34207

Downloads

Baixar Artigo 8 Downloads

Resumo

O TRABALHO VISA AVALIAR A INFLUÊNCIA DE DIFERENTES TEORES DE RESÍDUO NAS PROPRIEDADES FÍSICAS E MECÂNICAS DE UMA COMPOSIÇÃO TÍPICA DE CERÂMICA VERMELHA, A QUAL É COMERCIALIZADA EM CAMPOS DOS GOYTACAZES. O RESÍDUO É PROVENIENTE DA PRIMEIRA ETAPA DE FABRICAÇÃO DE VIDROS EM UM PROCESSO CONVENCIONAL DE TÊMPERA. CORPOS DE PROVA CERÂMICOS FORAM PREPARADOS COM INCORPORAÇÕES DE 0, 5, 10 E 20% DE RESÍDUO. AS AMOSTRAS FORAM OBTIDAS POR EXTRUSÃO, SECAS E QUEIMADAS EM 800, 900, 1000°C EM FORNO DE LABORATÓRIO. FORAM REALIZADAS ANÁLISES DAS MATÉRIAS-PRIMAS, DENTRE AS QUAIS SE PODEM DESTACAR AS MORFOLÓGICAS, FÍSICAS E QUÍMICAS, E POSTERIORMENTE FORAM REALIZADOS TESTES NAS PEÇAS CERÂMICAS QUEIMADAS. AS PROPRIEDADES OBTIDAS DE QUEIMA FORAM A DENSIDADE APARENTE A SECO, ABSORÇÃO DE ÁGUA E RETRAÇÃO LINEAR DE QUEIMA. OS RESULTADOS OBTIDOS DEMONSTRARAM QUE TANTO O AUMENTO DO TEOR DE VIDRO QUANTO O AUMENTO DA TEMPERATURA INFLUENCIARAM POSITIVAMENTE NAS PROPRIEDADES ESTUDADAS, E, ALÉM DISSO, O VIDRO ATUOU DE MODO A REDUZIR A TEMPERATURA ADEQUADA DE QUEIMA

 

THE WORK AIMS TO EVALUATE THE INFLUENCE OF DIFFERENT LEVELS OF RESIDUE ON THE PHYSICAL AND MECHANICAL PROPERTIES OF A TYPICAL COMPOSITION OF RED CERAMIC, WHICH IS MARKETED IN CAMPOS DOS GOYTACAZES, RIO DE JANEIRO. THE RESIDUE COMES FROM THE FIRST STAGE OF GLASS MANUFACTURING IN A CONVENTIONAL TEMPERING PROCESS. CERAMIC SPECIMENS WERE PREPARED WITH 0, 5, 10 AND 20% RESIDUE INCORPORATIONS. THE SAMPLES WERE OBTAINED BY EXTRUSION, DRIED AND FIRED AT 800, 900, 1000 ° C IN A LABORATORY OVEN. ANALYZES OF THE RAW MATERIALS WERE CARRIED OUT, AMONG WHICH THE MORPHOLOGICAL, PHYSICAL AND CHEMICAL ONES CAN BE HIGHLIGHTED, AND AFTERWARDS TESTS WERE CARRIED OUT ON THE FIRED CERAMIC SPECIMEN. THE FIRING PROPERTIES OBTAINED WERE DRY BULK DENSITY, WATER ABSORPTION, LINEAR FIRING SHRINKAGE. THE RESULTS OBTAINED DEMONSTRATED THAT BOTH THE INCREASE IN THE GLASS CONTENT AND THE INCREASE IN THE TEMPERATURE HAD POSITIVE EFFECTS ON THE STUDIED PROPERTIES, AND, IN ADDITION TO THAT, THE GLASS ACTED IN ORDER TO LOWER THE APPROPRIATE FIRING TEMPERATURE

Palavras-chave

Vidro Plano; Cerâmica Vermelha; Reciclagem; Resíduo

Flat Glass; Red Ceramic; Recycling; Residue