Título

INFLUÊNCIA DA ADIÇÃO DE BORO NA ESTRUTURA DO FERRO FUNDIDO BRANCO ALTO CROMO COM MOLIBDÊNIO, NO ESTADO BRUTO DE FUSÃO E TRATADO TERMICAMENTE

INFLUENCE OF BORON ADDITION ON THE STRUCTURE OF HIGH CHROMIUM WHITE CAST IRON WITH MOLYBDENUM IN THE MELT STATE AND HEAT TREATED

DOI

10.5151/1516-392X-30474

Downloads

Baixar Artigo 423 Downloads

Resumo

Os ferros fundidos brancos alto cromo (High Chromiun Cast Iron - HCCI) são ligas ferrosas com alta resistência ao desgaste. Isso se deve à elevada fração volumétrica de carbonetos eutéticos (10 - 30%) que é distribuída em uma matriz metálica constituída de austenita, martensita e carbonetos secundários. Nesse trabalho será estudado o efeito da adição de molibdênio e boro na estrutura dos HCCI. Para alcançar tal objetivo, inicialmente foram fundidas ligas de HCCI da classe ASTM 532 IIIA com e sem adição de boro (e adição de molibdênio em 1%). Posteriormente, as ligas foram tratadas termicamente passando por recozimento, têmpera (desestabilização) e revenimento. Após o tratamento térmico, as amostras foram analisadas por microscopia óptica e análise de difração de raios X (DRX). Os resultados indicam microestruturas refinadas para amostras com molibdênio e sem boro (BFMo) e formação de carbonetos primários grandes em amostras com adição de molibdênio e boro (BFMoB). Além disso, o tratamento térmico provocou um refinamento da microestrutura da liga TTMo e na liga TTMoB foi observada pequena quantidade de austenita retida. Sendo assim, a adição de boro provocou a formação de carbonetos primários (M7C3 - de maior tamanho) e secundários (M23C6, M3C) e promoveu a diminuição da quantidade de austenita retida.

 

High chromium cast iron (HCCI) are ferrous alloys with high wear resistance. This is due to the high volumetric fraction of eutectic carbides (10 - 30%) that is distributed in a metallic matrix consisting of austenite, martensite and secondary carbides. In this work the effect of the boron addition in the HCCI microstructure will be studied. To achieve this purpose, HCCI alloys of the ASTM 532 IIIA class were initially cast with and without boron addition (and molybdenum addition of 1%). Subsequently, the alloys were thermally treated by annealing, quenching (austenite destabilization) and tempering. After the heat treatment, the samples were analyzed by optical microscopy and X-ray diffraction (XRD) analysis. The results showed fine microstructures for samples with molybdenum and without boron (BFMo) and formation of large primary carbides in samples with boron addition (BFMoB). In addition, the heat treatment resulted in a refinement of TTMo alloy microstructure and in the TTMoB alloy was observed small amount of retained austenite. Thus, the addition of boron caused the formation of primary (M7C3) and secondary carbides (M23C6, M3C) and led to a decrease of the amount of retained austenite.

Palavras-chave

Ferro fundido branco, Boro, Carbonetos, Microestrutura.

White cast iron, Boron, Carbides, Microstructure.

Como citar

Antônio, Loudiana Mosqueira; Pacheco, Dimas de Andrade; Oliveira, Cláudio Gonçalves de; Silva, Laura de Lima e; Godoy, Cristina; Pinheiro, Ivete Peixoto. INFLUÊNCIA DA ADIÇÃO DE BORO NA ESTRUTURA DO FERRO FUNDIDO BRANCO ALTO CROMO COM MOLIBDÊNIO, NO ESTADO BRUTO DE FUSÃO E TRATADO TERMICAMENTE , p. 1420-1428. In: 72nd ABM Annual Congress, São Paulo, 2017.