INFLUÊNCIA DA GRANULOMETRIA DA LAMA VERMELHA NAS PROPRIEDADES MECÂNICAS E DE FLAMABILIDADE DOS COMPÓSITOS: INFLUENCE OF RED MUD GRANULOMETRY ON THE MECHANICAL PROPERTIES AND FLAMMABILITY OF COMPOSITES

Buscando a reutilização de resíduos sólidos, o presente trabalho produziu compósitos de resina polimérica utilizando o resíduo industrial de Lama Vermelha (LV), proveniente da mineradora Hydro Alunorte (Pará), para avaliar suas propriedades mecânicas e de flamabilidade. As granulometrias empregadas foram de 0, 100 e 200 mesh, com as proporções de 10 % e 20 % para cada uma. Fez-se uso da resina poliéster insaturada isoftálica, atrelada ao iniciador e o acelerador de Cobalto nas proporções de 1 % e 1,5 %, em v/v, respectivamente. Para a fabricação dos compósitos utilizou-se o método manual “hand lay up” em moldes metálicos. Realizaram-se os ensaios de tração, físicos e de retardância a chama conforme as normas ASTM D 3039, NBR 12766 e ASTM D 635, respectivamente. Os resultados de resistência à tração foram satisfatórios à medida que se diminuiu a granulometria, o melhor deles com a composição de 10 % 100# atingindo 40,35 Mpa de resistência. A resistência à chama foi influenciada beneficamente, também, diminuindo-se a granulometria, e a menor taxa de queima se deu com a composição de 20 % 200# com 16,16 mm/min. Os resultados dos ensaios físicos (PA, AA, MEA) variaram de acordo com as proporções e granulometrias.

Seeking the reuse of solid residues, the present work produced polymeric resin compounds using the industrial residue of Red Mud, from the mining company Hydro Alunorte (Pará), with its mechanical properties of flammability. The granulometries employed were 0, 100 and 200 mesh, with proportions of 10% and 20% for each. Isophthalic unsaturated polyester resin was used, coupled to the initiator and the Cobalt accelerator in proportions of 1 % and 1,5 %, in v/v, respectively. The manual method “hand lay up” was used to manufacture the composites in metal molds. Traction, physical and flamel retardance tests were performer according to ASTM D 3039, NBR 12766 and ASTM D 635, respectively. The results of the traction resistance were satisfactory as the granulometry decreased, the best with the composition of 10 % 100# reaching 40.35 MPa of resistance. The flame resistance was also beneficially influenced by decreasing the granulometry, and the lowest burning rate that was made with the composition of 20 % 200# 16,16 mm/min. The results of the physical tests (PA, AA, MEA) varied according to the proportions and granulometry.

Palavras-chave

lAMA Vermelha; Granulometria, Resistência à Chama; Tração.

Red Mud; Granulometry; Flame Resistance; Traction.

Como citar

Santos, Eryck Eduardo Simplicio dos; Ferreira, Victor Hugo Mafra Monfredo; Daniel, Brenda Thayssa Figueira; Mendes, Bruno Henrique Alves; Costa, Deibson Silva da. INFLUÊNCIA DA GRANULOMETRIA DA LAMA VERMELHA NAS PROPRIEDADES MECÂNICAS E DE FLAMABILIDADE DOS COMPÓSITOS , p. 2634-2645. In: 74º Congresso Anual da ABM, São Paulo, 2019.
ISSN: 2594-5327 , DOI 10.5151/2594-5327-33739