Título

INFLUÊNCIA DA VARIAÇÃO DE TEMPERATURA DE RECOZIMENTO ENTRE 350 E 650ºC NAS PROPRIEDADES ESTRUTURAIS, FÍSICAS E MECÂNICAS DE UMA LIGA TINI RICA EM TI

THE INFLUENCE OF ANNEALING TEMPERATURE CHANGES BETWEEN 350 TO 650ºC ON STRUCTURAL, PHYSICAL AND MECHANICAL PROPERTIES OF A TI-RICH TINI ALLOY ANNEALED BETWEEN 350 AND 650ºC

Autoria

Alves, Andréy Escala; Matlakhova, Lioudmila Aleksandrovna; Júnior, Herval Ramos Paes; Carvalho, Eduardo Atem de; Palii, Natalia Alekseevna

DOI

10.5151/2594-5327-34184

Downloads

Baixar Artigo 9 Downloads

Resumo

FOI ESTUDADA A INFLUÊNCIA DA VARIAÇÃO DA TEMPERATURA DE RECOZIMENTO (350ºC, 450ºC, 550ºC E 650ºC) NA ESTRUTURA, PROPRIEDADES MECÂNICAS E ELÉTRICAS DE UMA LIGA TINI (51,6%AT. TI), POSTERIORMENTE TEMPERADA EM ÁGUA FRIA. A DIFRAÇÃO DE RAIOS X REVELOU A PRESENÇA DAS FASES DE MARTENSITA B19´ E TI2NI EM TODAS AS AMOSTRAS, ANTES E APÓS DEFORMAÇÃO. A FASE INTERMEDIÁRIA R FOI IDENTIFICADA APÓS A TÊMPERA A PARTIR DE 350ºC, 450ºC E 550ºC E APÓS DEFORMAÇÃO DE AMOSTRA RECOZIDA EM 650ºC. A FASE DE ALTA TEMPERATURA B2 FOI IDENTIFICADA APÓS RECOZIMENTO EM 550ºC E 650ºC. A MELHOR RELAÇÃO DE DEFORMAÇÃO ACUMULADA (6,1%) ALIADA À ELEVADA RESISTÊNCIA À COMPRESSÃO (2845MPA) FOI OBTIDA NA AMOSTRA RECOZIDA EM 550ºC. A RESISTIVIDADE ELÉTRICA APRESENTOU VARIAÇÕES ENTRE 70,9 E 78,5 10-6Ω.CM NA CONDIÇÃO NÃO-DEFORMADA, RESULTADO DA DIFERENTE PARTICIPAÇÃO DAS FASES NA ESTRUTURA APÓS TÊMPERA. COM DEFORMAÇÃO ATÉ 10%, FOI OBSERVADA UMA REDUÇÃO DESSA GRANDEZA PARA A FAIXA ENTRE 59,9 E 71,7 10-6Ω.CM DEVIDO À TRANSFORMAÇÃO R->B19’ INDUZIDA POR TENSÃO. ASSIM, FOI CONSTADA UMA SENSIBILIDADE DAS LIGAS TINI RICAS EM TI À VARIAÇÕES DE TRATAMENTO TÉRMICO APLICADO.

 

THE INFLUENCE OF ANNEALING TEMPERATURE VARIATION (350ºC, 450ºC, 550ºC AND 650ºC) FOLLOWED BY COLD WATER QUENCHING ON THE STRUCTURE, MECHANICAL PROPERTIES AND ELECTRICAL RESISTIVITY OF A TINI ALLOY (51.6 AT.%TI) WAS INVESTIGATED. X-RAY DIFFRACTION REVEALED THE PRESENCE OF B19´ AND TI2NI PHASES PRIOR AND AFTER DEFORMATION. THE INTERMEDIATE PHASE R WAS IDENTIFIED AFTER QUENCHING AT 350ºC, 450ºC AND 550ºC AND AFTER DEFORMATION OF THE SAMPLE ANNEALED AT 650ºC. THE HIGH TEMPERATURE PHASE B2 WAS IDENTIFIED AFTER HEAT TREATMENT AT 550ºC AND 650ºC. THE BEST ACCUMULATED STRAIN RATIO (6.1%) COMBINED WITH HIGH COMPRESSIVE STRENGTH (2845MPA) WAS OBTAINED IN THE SAMPLE ANNEALED AT 550ºC. THE ELECTRICAL RESISTIVITY VARIED BETWEEN 70.9 AND 78.5 10-6Ω.CM IN THE NON-DEFORMED CONDITION, RESULTING FROM THE DIFFERENT PARTICIPATION OF THE PHASES IN THE STRUCTURE AFTER QUENCHING. A DECREASE IN ELECTRICAL RESISTIVITY WAS OBSERVED AFTER MECHANICAL DEFORMATION TO 59.9 AND 71.7 10-6Ω.CM DUE TO THE STRESS-INDUCED TRANSFORMATION R->B19'. THUS, TI-RICH TINI ALLOYS SEEM TO BE SENSITIVE TO DIFFERENT HEAT TREATMENT APPLIED.

Palavras-chave

LIGA TINI; TRATAMENTO TÉRMICO; ESTRUTURA; PROPRIEDADES.

TINI ALLOY; HEAT TREATMENT; STRUCTURE; PROPERTIES.