O OBJETIVO DESTE TRABALHO FOI ADICIONAR BLANDS DE UM RESíDUO DITO COMBUSTíVEL (CASCA DE JABUTICABA) E UM RESíDUO FUNDENTE (VIDRO DE EMBALAGENS) EM UMA MASSA CERâMICA AVALIANDO AS PROPRIEDADES DAS CERâMICAS QUEIMADAS. A MASSA CERâMICA E O VIDRO FORAM CARACTERIZADAS POR FRX E DRX. AS MATéRIAS-PRIMAS FORAM SECAS E PENEIRADAS PARA QUE FOSSEM FEITAS AS FORMULAçõES COM DIFERENTES PERCENTUAIS E MISTURAS DOS RESíDUOS. FORAM PRODUZIDOS CORPOS DE PROVA COM 114 X 25,0 X 11,0 MM COM PRESSãO DE 10TON, E QUEIMADOS NA TEMPERATURA DE 950°C. APóS, FORAM AVALIADAS AS PROPRIEDADES DE: ABSORçãO DE áGUA, RETRAçãO LINEAR, E TENSãO DE RUPTURA à FLEXãO POR TRêS PONTOS. COM OS RESULTADOS OBTIDOS OBSERVOU QUE POR SE TRATAR DE UM RESíDUO COM GRANDE QUANTIDADE DE MATéRIA ORGâNICA, SOZINHA A CASCA DE JABUTICABA PREJUDICARIA AS PROPRIEDADES DAS CERâMICAS, DEVENDO APENAS SER UTILIZADA EM QUANTIDADES PEQUENAS. QUANDO FORAM FEITOS BLANDS COM OS DOIS RESíDUOS, MESMO QUEIMANDO EM TEMPERATURAS MAIS BAIXAS, HOUVE UMA MELHORA NOS RESULTADOS. COM ISTO, é POSSíVEL CONCLUIR QUE A INCORPORAçãO DA MISTURA DOS DOIS RESíDUOS EM CERâMICA é UMA ALTERNATIVA MUITO VANTAJOSA, TANTO DO PONTO AMBIENTAL, PARA A DESTINAçãO DESTES RESíDUOS, QUANTO PARA A INDúSTRIA CERâMICA, ONDE ALéM DE MELHORIA DA QUALIDADE DAS PEçAS, TEM ECONOMIA DE ENERGIA NO PROCESSO DA QUEIMA
THE OBJECTIVE OF THIS WORK WAS TO ADD BLANDS OF A SO-CALLED COMBUSTIBLE WASTE (JABUTICABA BARK) AND A FLUX WASTE (PACKAGING GLASS) IN A CERAMIC MASS, EVALUATING THE PROPERTIES OF FIRED CERAMICS. THE CERAMIC MASS AND THE GLASS WERE CHARACTERIZED BY XRF AND XRD. THE RAW MATERIALS WERE DRIED AND SIEVED SO THAT FORMULATIONS COULD BE MADE WITH DIFFERENT PERCENTAGES AND MIXTURES OF WASTE. SPECIMENS MEASURING 114 X 25.0 X 11.0 MM WERE PRODUCED WITH A PRESSURE OF 10TON, AND FIRED AT TEMPERATURE OF 950°C. AFTERWARDS, THE FOLLOWING PROPERTIES WERE EVALUATED: WATER ABSORPTION, LINEAR SHRINKAGE, AND THREE-POINT FLEXURAL STRENGTH. WITH THE RESULTS OBTAINED, IT WAS OBSERVED THAT BECAUSE IT IS A WASTE WITH A LARGE AMOUNT OF ORGANIC MATTER, THE JABUTICABA PEEL ALONE WOULD HARM THE PROPERTIES OF CERAMICS, AND SHOULD ONLY BE USED IN SMALL QUANTITIES. WHEN BLANDS WERE MADE WITH THE TWO WASTE, EVEN BURNING AT LOWER TEMPERATURES, THERE WAS A SIGNIFICANT IMPROVEMENT. WITH THIS, IT IS POSSIBLE TO CONCLUDE THAT THE INCORPORATION OF THE MIXTURE OF THE TWO WASTES IN CERAMICS IS A VERY ADVANTAGEOUS ALTERNATIVE, BOTH FROM THE ENVIRONMENTAL POINT OF VIEW, FOR THE DISPOSAL OF THESE WASTES, AND FOR THE CERAMIC INDUSTRY, WHERE IN ADDITION TO IMPROVING THE QUALITY OF THE PIECES, IT HAS SAVINGS ENERGY IN THE BURNING PROCESS
Palavras-chave
Resíduo de Jabuticaba; Incorporação; Vidro de embalagem; Cerâmica
Jabuticaba waste; Packaging glass; Incorporation; Ceramics.
Como citar
CABRAL, MATHEUS MARINHO;
FERREIRA, ELVIS PANTALEÃO;
VIEIRA, CARLOS MAURÍCIO FONTES;
DELAQUA, GEOVANA CARLA GIRONDI.
INFLUÊNCIA DE MISTURAS DE RESÍDUOS FUNDENTE E COMBUSTÍVEL NAS PROPRIEDADES CERÂMICAS
,
p. 2680-2690.
In: 77º Congresso Anual da ABM - Internacional,
São Paulo, Brasil,
2024.
ISSN: 2594-5327
, DOI 10.5151/2594-5327-41280