INFLUÊNCIA DO CROMO NAS PROPRIEDADES MECÂNICAS E METALÚRGICAS DO AÇO SAE1040

INFLUENCE OF CHROMIUM MECHANICAL AND METALLURGICAL PROPERTIES OF STEEL SAE 1040

DOI

10.5151/1516-392X-25008

Downloads

Baixar Artigo 819 Downloads

Resumo

Os aços carbono são materiais metálicos muito importantes na fabricação de peças para a indústria metal-mecânica. Parafusos, hastes, eixos, pistões, engrenagens são fabricados a partir desse tipo de aço, mais especificamente do aço SAE1040. O objetivo desse trabalho foi de avaliar a influência da presença de 0,2% em massa de cromo nas propriedades mecânicas e metalúrgicas de um aço com 0,4% em massa de carbono. A liga padrão SAE1040 e esta liga modificada com cromo foram submetidas a tratamentos térmicos de normalização, recozimento, têmpera e revenimento, e comparadas às durezas e microdurezas das diferentes amostras entre si. Os resultados obtidos evidenciaram que a adição de cromo é um método eficiente quando se deseja aumentar a resistência de um material. Observou-se que os valores de dureza e microdureza para o aço com a adição de cromo apresentaram-se maiores em relação ao aço padrão, como consequência das microestruturas obtidas, principalmente após têmpera e revenimento. A adição de 0,2% em massa de cromo no aço carbono influiu na melhora das propriedades mecânicas do aço tornando-o mais interessante na fabricação de peças para a indústria metal-mecânica.

 

Carbon steels are very important materials in parts production to the metal-mechanical industry. Screws, rods, shafts, pistons, gears are manufactured to this kind of steel, more specifically SAE1040 steel. The objective of this study was to evaluate the influence of the presence of 0.2wt% of chromium in the mechanical and metallurgical properties of steel with 0.4wt% carbon. The standard alloy SAE1040 and this alloy modified by chromium were submitted to heat treatment of normalization, annealing, quenching and tempering, and was compared to the hardness and microhardness of different samples to each other. The results showed that the addition of chromium is an efficient method when you want to increase the resistance a material. It was observed that the values for hardness and microhardness for the steel with the addition of chromium were bigger in relation to standard steel, it because of the microstructures obtained after quenching and tempering. The addition of 0.2wt% of chromium in carbon steel influenced the improvement of mechanical properties of steel, making it more interesting for the manufacture of parts for the metalworking industry.

Palavras-chave

Cromo; Tratamento térmico; SAE1040; Ensaios mecânicos; Aço

Chromium, Heat treatment; Standard alloy; SAE1040; Mechanical tests; Steel

Como citar

Marcos Vinícios de Souza; Thalles Vinícios Morais Caldeira; Larissa de Barros Machado Vilela; Roney Eduardo Lino; Leandro Aparecido Marchi; João Bosco dos Santos; Ricardo Luiz Perez Teixeira. INFLUÊNCIA DO CROMO NAS PROPRIEDADES MECÂNICAS E METALÚRGICAS DO AÇO SAE1040 , p. 8618-8628. In: 69° Congresso Anual da ABM - Internacional, São Paulo - Brasil, 2014.