Título

INFLUÊNCIA DO ENVELHECIMENTO NO DESEMPENHO BALÍSTICO DE UM COMPÓSITO DE ARAMIDA

INFLUENCE OF AGING ON BALLISTIC PERFORMANCE OF AN ARAMID COMPOSITE

DOI

10.5151/2594-5327-23187

Downloads

Baixar Artigo 137 Downloads

Resumo

A necessidade de materiais de alta resistência e elevada tenacidade para emprego em proteções balísticas, tem levado ao desenvolvimento de materiais compósitos de matriz polimérica reforçados com fibras. Todavia, os materiais poliméricos quando expostos à agentes ambientais podem apresentar alterações que, frequentemente, modificam as suas propriedades. No presente trabalho foi estudado o desempenho balístico de um laminado de tecido de aramida com policloropreno (CR) envelhecido artificialmente por irradiação gama, em uma faixa de doses entre 40 kGy e 200 kGy. O compósito, antes e após irradiação gama, foi caracterizado por meio de ensaios físico-químicos (TGA, DSC e FTIR) e mecânicos (tração e adesão) e submetido a teste balístico. Os resultados obtidos mostraram que a irradiação gama produz degradação da poliaramida, a qual apresenta cisão da cadeia. Todavia, verificou-se que o envelhecimento por irradiação gama, nas doses utilizadas no presente trabalho, teve pouca influência no desempenho balístico do material, mostrando que o comportamento mecânico do compósito pode ter sido influenciado pela textura do tecido.

 

The need for materials of high strength and high toughness for use in ballistic protection has led to the development of polymer matrix composites (PMCs) reinforced with fibers. However, polymeric materials when exposed to environmental agents may show changes that often modify their properties. In the present work, the ballistic performance of a laminate made of aramid fabric and polychloroprene (CR), artificially aged by gamma irradiation in a range of doses between 40 kGy and 200 kGy was studied. The material, before and after gamma irradiation, was characterized by physico-chemical (TGA, DSC and FTIR) and mechanical (tensile and adhesion)and subjected to ballistic test. The results showed that the gamma irradiation produces degradation of polyaramide, which presents chain scission. However, it was found that gamma irradiation aging at doses used in this study had small effect on the ballistic performance of the material, showing that the mechanical behavior of the composite may have been influenced by the fabric texture.

Palavras-chave

Aramida; Policloropreno; Blindagem balística; Envelhecimento; Irradiação gama.

Aramid; Polychloroprene; Ballistic armor; Aging; Gamma irradiation.