INFLUÊNCIA DO REVENIMENTO NA DUREZA E NA MICROESTRUTURA DE UM AÇO SAE 4340

INFLUENCE OF COATING ON THE HARDNESS AND MICROSTRUCTURE OF A SAE 4340 STEEL

Autoria

Souza, Victor Barbosa de; Freire, Alan Almeida; Araújo, Caio Sergio Friaça Lopes de; Cerqueira, Niander Aguiar; Gallo, Daniel Passos; Lima, Amanda Camerini; Azevedo, Afonso Rangel Garcez de; Marvila, Markssuel Teixeira; Monteiro, Sergio Neves; Miguel, Thais Pirovane

DOI

10.5151/2594-5327-34052

Downloads

Baixar Artigo 8 Downloads

Resumo

A PRESENTE PESQUISA AVALIOU A INFLUÊNCIA DO TRATAMENTO DE REVENIMENTO NA DUREZA E NA MICROESTRUTURA DO AÇO SAE 4340, COM OBJETIVO DE CONSTATAR A IMPORTÂNCIA DO REVENIMENTO PARA A INDÚSTRIA E ANALISAR QUAIS ALTERAÇÕES QUE ESTE TRATAMENTO PROVOCA NO MATERIAL. PARA A REALIZAÇÃO DESTE TRABALHO FORAM SUBMETIDAS AO TRATAMENTO DE TÊMPERA, E LOGO EM SEGUIDA AO REVENIMENTO, AMOSTRAS DO AÇO, TENDO OS RESULTADOS MOSTRADO QUE A TÊMPERA CAUSOU AUMENTO NA DUREZA E, DEVIDO AO FATO DE SER UM MATERIAL COM BOA TEMPERABILIDADE, HOUVE A FORMAÇÃO DE MERTENSITA NA SUA MICROESTRUTURA, COMPROVADA PELA ANÁLISE METALOGRÁFICA. ENTRETANTO A TÊMPERA DEIXA O MATERIAL MUITO FRÁGIL, O QUE LIMITA SUA APLICAÇÃO NA INDÚSTRIA. APÓS A REALIZAÇÃO DO TRATAMENTO DE REVENIMENTO E NOVA REALIZAÇÃO DOS ENSAIOS DE DUREZA, FOI OBSERVADA UMA REDUÇÃO SIGNIFICATIVA DESTA PROPRIEDADE QUE, CONSEQUENTEMENTE, RECUPEROU PARTE DE SUA TENACIDADE E DUCTILIDADE, MOSTRANDO A IMPORTÂNCIA DESTE TRATAMENTO PARA APLICAÇÃO DO AÇO SAE 4340 NA INDÚSTRIA. FOI REALIZADA UMA ANÁLISE COMPARATIVA DA DUREZA DO AÇO ANTES E APÓS O TRATAMENTO TÉRMICO, QUE POSSIBILITOU A VERIFICAÇÃO DAS ALTERAÇÕES QUE O TRATAMENTO DE REVENIMENTO PROVOCA ATRAVÉS NO AÇO SAE 4340 POR MEIO DO ENSAIO METALOGRÁFICO.

 

THE PRESENT RESEARCH EVALUATED THE INFLUENCE OF TEMPERING TREATMENT ON THE HARDNESS AND MICROSTRUCTURE OF SAE 4340 STEEL, WITH THE OBJECTIVE OF VERIFYING THE IMPORTANCE OF TEMPERING FOR THE INDUSTRY AND ANALYZING WHAT CHANGES THIS TREATMENT CAUSES IN THE MATERIAL. IN ORDER TO CARRY OUT THIS WORK, SAMPLES OF THE STEEL WERE SUBJECTED TO THE QUENCHING TREATMENT, AND RIGHT AFTER THE TEMPERING, THE RESULTS SHOWED THAT THE QUENCHING CAUSED AN INCREASE IN HARDNESS AND, DUE TO THE FACT THAT IT WAS A MATERIAL WITH GOOD TEMPERABILITY, THERE WAS THE FORMATION MERTENSITE IN ITS MICROSTRUCTURE, PROVEN BY METALLOGRAPHIC ANALYSIS. HOWEVER, TEMPERING LEAVES THE MATERIAL VERY FRAGILE, WHICH LIMITS ITS APPLICATION IN THE INDUSTRY. AFTER THE TEMPERING TREATMENT AND THE NEW HARDNESS TESTS, A SIGNIFICANT REDUCTION IN THIS PROPERTY WAS OBSERVED, WHICH CONSEQUENTLY RECOVERED PART OF ITS TOUGHNESS AND DUCTILITY, SHOWING THE IMPORTANCE OF THIS TREATMENT FOR THE APPLICATION OF SAE 4340 STEEL IN THE INDUSTRY. A COMPARATIVE ANALYSIS OF THE HARDNESS OF THE STEEL WAS CARRIED OUT BEFORE AND AFTER THE HEAT TREATMENT, WHICH ENABLED THE VERIFICATION OF THE CHANGES THAT THE TEMPERING TREATMENT CAUSES IN THE SAE 4340 STEEL THROUGH THE METALLOGRAPHIC TEST.

Palavras-chave

Tratamento Térmico; Revenimento; Dureza; Aço SAE 4340

Heat treatment; Tempering; Toughness; SAE 4340 steel