INFLUÊNCIA DOS ATIVADORES NA GEOPOLIMERIZAÇÃO COM PRECURSOR DE CINZA VOLANTE

INFLUENCE OF ACTIVATORS ON GEOPOLYMERIZATION WITH FLY ASH PRECURSOR

DOI

10.5151/2594-5327-40611

Downloads

Baixar Artigo 1 Downloads

Resumo

O GEOPOLíMERO é UM MATERIAL DESENVOLVIDO ATRAVéS DA ATIVAçãO ALCALINA DE UM PRECURSOR RICO EM ALUMINOSSILICATOS, COMO SIO2 E AL2O3, EM UMA POLIMERIZAçãO. A PRODUçãO DE CIMENTO GEOPOLIMéRICO REQUER UM MATERIAL DE ALUMINOSSILICATO, UM REAGENTE ALCALINO (COMO SILICATOS SOLúVEIS DE SóDIO OU POTáSSIO), E áGUA. EXISTEM DOIS TIPOS PRINCIPAIS DE ATIVADORES UTILIZADOS NA SíNTESE: SOLUçõES DE HIDRóXIDOS ALCALINOS OU UMA MISTURA DE SOLUçõES DE SILICATO ALCALINO E HIDRóXIDO ALCALINO. O ESTUDO PROPOSTO VISA ANALISAR GEOPOLíMEROS FABRICADOS COM PRECURSOR DE CINZA VOLANTE E DIFERENTES ATIVADORES ALCALINOS PARA ENTENDER A ATIVAçãO MAIS ADEQUADA PARA O PRECURSOR ESPECíFICO. OS ENSAIOS DE ESTADO FRESCO INDICARAM QUE A MASSA ATIVADA COM HIDRóXIDO DE SóDIO E SILICATO DE SóDIO é MAIS DENSA, VISCOSA, JUSTAMENTE PELA PRESENçA DO SILICATO DE SóDIO. O GEOPOLíMERO ATIVADO COM HIDRóXIDO DE SóDIO APRESENTOU MAIOR RESISTêNCIA à COMPRESSãO DO QUE O GEOPOLíMERO ATIVADO POR HIDRóXIDO DE POTáSSIO, O QUE Já ERA ESPERADO CONSIDERANDO OS RESULTADOS ENCONTRADOS NOS ENSAIOS DE ESTADO FRESCO. OS GEOPOLíMEROS ATIVADOS COM HIDRóXIDO DE SóDIO APRESENTARAM UMA MICROESTRUTURA MENOS POROSA. PORTANTO, PARA O ESTUDO PROPOSTO, O MELHOR ATIVADOR ENCONTRADO FOI O ATIVADOR DE SILICATO E HIDRóXIDO DE SóDIO, COM UMA MOLARIDADE DE 7.

 

GEOPOLYMER IS A MATERIAL DEVELOPED THROUGH THE ALKALINE ACTIVATION OF A PRECURSOR RICH IN ALUMINOSILICATES, SUCH AS SIO2 AND AL2O3, IN A POLYMERIZATION. THE PRODUCTION OF GEOPOLYMER CEMENT REQUIRES AN ALUMINOSILICATE MATERIAL, AN ALKALINE REAGENT (SUCH AS SOLUBLE SODIUM OR POTASSIUM SILICATES), AND WATER. THERE ARE TWO MAIN TYPES OF ACTIVATORS USED IN SYNTHESIS: ALKALI HYDROXIDE SOLUTIONS OR A MIXTURE OF ALKALI SILICATE AND ALKALI HYDROXIDE SOLUTIONS. THE PROPOSED STUDY AIMS TO ANALYZE GEOPOLYMERS MANUFACTURED WITH FLY ASH PRECURSOR AND DIFFERENT ALKALINE ACTIVATORS TO UNDERSTAND THE MOST APPROPRIATE ACTIVATION FOR THE SPECIFIC PRECURSOR. FRESH STATE TESTS INDICATED THAT THE MASS ACTIVATED WITH SODIUM HYDROXIDE AND SODIUM SILICATE IS DENSER AND MORE VISCOUS, PRECISELY DUE TO THE PRESENCE OF SODIUM SILICATE. THE GEOPOLYMER ACTIVATED WITH SODIUM HYDROXIDE SHOWED GREATER COMPRESSIVE STRENGTH THAN THE GEOPOLYMER ACTIVATED WITH POTASSIUM HYDROXIDE, WHICH WAS ALREADY EXPECTED CONSIDERING THE RESULTS FOUND IN THE FRESH STATE TESTS. THEREFORE, FOR THE PROPOSED STUDY, THE BEST ACTIVATOR FOUND WAS THE SILICATE AND SODIUM HYDROXIDE ACTIVATOR, WITH A MOLARITY OF 7.

Palavras-chave

Ativação alcalina; Geopolímeros; Cinza volante.

Alkaline activation; Geopolymers; Fly ash.

Como citar

RISCADO, ANA LAURA LOPES DE MATOS; MARVILA, MARKSSUEL TEIXEIRA; VIEIRA, CARLOS MAURÍCIO FONTES; AZEVEDO, AFONSO RANGEL GARCEZ DE; SILVA, SHEILA MARA SANTOS DA. INFLUÊNCIA DOS ATIVADORES NA GEOPOLIMERIZAÇÃO COM PRECURSOR DE CINZA VOLANTE , p. 927-936. In: 77º Congresso Anual da ABM - Internacional, São Paulo, Brasil, 2024.