INFLUÊNCIA DOS PARÂMETROS DE SOLDAGEM NA RESISTÊNCIA À CORROSÃO DE CHAPAS DE AÇO GALVANIZADAS UTILIZANDO MIG BRAZING: INFLUENCE OF WELDING PARAMETERS ON RESISTANCE TO CORROSION OF GALVANIZED STEEL SHEETS USING MIG BRAZING

O OBJETIVO DESTE TRABALHO FOI ANALISAR A RESISTÊNCIA À CORROSÃO DE CHAPAS DE AÇO GALVANIZADO SUBMETIDOS AO PROCESSO DE SOLDAGEM DO TIPO BRASAGEM MIG (MIG BRAZING). AS AMOSTRAS FORAM SOLDADAS COM UMA REGULAGEM DE FONTE ESPECÍFICA (CORRENTE CONTÍNUA OU ALTERNADA) PARA CHAPA GALVANIZADA E OUTRA CONVENCIONAL, CADA PROCESSO COM TRÊS VARIAÇÕES DE VELOCIDADE (300, 500 E 800 MM/S) FORAM MEDIDAS E ANALISADAS AS ESPESSURAS DA CAMADA DE ZINCO NA REGIÃO AFETADA PELA SOLDA, E CARACTERIZOU-SE A MICROESTRUTURA POR MICROSCOPIA ÓPTICA APÓS PREPARAÇÃO METALOGRÁFICA. NESSAS AMOSTRAS TAMBÉM FORAM ESTUDADAS AS MODIFICAÇÕES ESTRUTURAIS INDUZIDAS NA ZONA TERMICAMENTE AFETADA (ZTA) PELO PROCESSO ALÉM DA REALIZAÇÃO DE SALT SPRAY. OS RESULTADOS MOSTRARAM QUE, COM CORRENTE CONTÍNUA, O EFEITO DA CORROSÃO NAS AMOSTRAS TESTADAS FOI MAIOR QUE NAS CHAPAS QUE FORAM SOLDADAS NA CONDIÇÃO DE CORRENTE ALTERNADA. ESSES RESULTADOS FORAM CORROBORADOS PELA ANÁLISE MICROESTRUTURAL QUE MOSTROU OS EFEITOS DA SOLDAGEM COM O ESTUDO DA ZTA E A INFLUÊNCIA DA CAMADA DE ZINCO DA CHAPA.

THE GOAL OF THIS WORK WAS TO ANALYZE THE CORROSION RESISTANCE OF MIG BRAZING TYPE WELDING ON GALVANIZED STEEL PLATES. SAMPLES WERE WELDED WITH A SPECIFIC SOURCE REGULATION FOR BOTH GALVANIZED PLATES AND CONVENTIONAL ONES, EACH WITH THREE WELDING SPEED VARIATIONS (300, 500 AND 800 MM/S). THE THICKNESS OF THE ZINC LAYER IN THE REGION AFFECTED BY THE WELD WAS MEASURED AND ANALYZED; LIKEWISE, OPTICAL MICROSCOPY WAS CONDUCTED ON SAMPLES METALLOGRAPHICALLY PREPARED. IN THESE SAMPLES, THE STRUCTURAL MODIFICATIONS INDUCED IN THE HEAT AFFECTED ZONE (HAZ) BY THE PROCESS WERE ALSO STUDIED, IN ADDITION TO THE SALT SPRAY. THE RESULTS SHOWED THAT, WITH DIRECT CURRENT, THE EFFECT OF CORROSION IN THE SAMPLES TESTED WAS GREATER THAN IN THE PLATES THAT WERE WELDED UNDER ALTERNATING CURRENT, BEING CORROBORATED BY MICROSTRUCTURAL ANALYSIS THAT SHOWED THE EFFECTS OF WELDING WITH THE STUDY OF HAZ AND THE ZINC LAYER OF THE PLATE.

Palavras-chave

Mig Brazing; Resistência à Corrosão; Chapa galvanizada.

Mig Brazing, Corrosion resistance, Galvanized steel plates.

Como citar

Seriacopi, Vanessa; Auricchio, Paulo de Souza Chohfi; Lebrão, Susana Marraccini Giampietri; Farias, Adalto de; Bordinassi, Éd Cláudio; Moraes, Viviane Tavares de. INFLUÊNCIA DOS PARÂMETROS DE SOLDAGEM NA RESISTÊNCIA À CORROSÃO DE CHAPAS DE AÇO GALVANIZADAS UTILIZANDO MIG BRAZING , p. 203-213. In: 75° Congresso Anual da ABM, São Paulo, 2022.
ISSN: 2594-5327 , DOI 10.5151/2594-5327-34281