Título

INVESTIGAÇÃO DOS MÉTODOS DE DETERMINAÇÃO DA TEMPERATURA DE TRANSIÇÃO DÚCTIL-FRÁGIL (TTDF) UTILIZANDO ENSAIO DE IMPACTO CHARPY

INVESTIGATION OF METHODS FOR DBTT DETERMINATION BY USING CHARPY IMPACT TESTING

Autoria

Kátia Cristina Gouveia; Rodrigo Magnabosco

Kátia Cristina Gouveia

Eu sou esse autor

Rodrigo Magnabosco

Eu sou esse autor

DOI

10.5151/1516-392X-24409

Downloads

Resumo

O objetivo deste trabalho foi determinar a TTDF do aço ASTM A36 com diferentes graus de encruamento após ensaios de impacto Charpy, sob diversas metodologias. Não se notaram diferenças no comportamento do material quando se avaliam os valores de TTDF obtidos pela medição da expansão lateral dos corpos de prova, nem considerando o valor da TTDF na qual o material apresenta 50% de fratura frágil, usando as metodologias de avaliação visual das faces de fratura dos corpos de prova, embora os valores sejam divergentes dos valores obtidos pelos métodos analíticos. A avaliação das faces de fratura dos corpos de prova por microscopia eletrônica de varredura permitiu visualizar que nas regiões onde visualmente considerou-se que havia apenas fratura frágil, também haviam regiões típicas de fratura dúctil. Conclui-se que a metodologia mais indicada é aquela que considera a TTDF como a temperatura na qual a energia absorvida é a média dos patamares superior e inferior, pois é um método simples, de fácil reprodutibilidade e que melhor refletiu a tendência de comportamento do material nos diferentes graus de encruamento estudados.

The purpose of this work was to define ASTM A-36 steel DBTT, presenting various pre-strain levels, after Charpy impact testing, by using several methodologies, evaluating its validity. When DBTT values were obtained from lateral expansion, it was not possible to notice any relation with pre-strain, neither when DBTT values were defined as the temperature where 50% of brittle fracture was determined, for both quantitative and qualitative methods of evaluation, although these values are different from analytical results. When fractures were evaluated by scanning electron microscopy, and it was possible to visualize that in the portions where, from visual analysis, it was considered that a brittle fracture occurs, there are also plastic deformation, which means that a ductile fracture also occurs. It was concluded that the most indicate methodology for DBTT determination is the one at which absorbed energy is the average between superior and inferior energy plateaus, since it is easy to be done and to be reproduced, and it is the one that better reflects material behavior for the adopted pre-strain levels.

Palavras-chave

Ensaio Charpy; TTDF; Fratura frágil; Fratura dúctil

Charpy test; DBTT; Brittle fracture; Ductile fracture