MELHORIA DO DESEMPENHO OPERACIONAL E DA QUALIDADE DAS PLACAS DE BAIXO CARBONO LIGADOS AO AL E SI PARA APLICAÇÕES ELÉTRICAS

IMPROVEMENT OF OPERATIONAL AND QUALITY PERFORMANCE IN THE CASTING SLABS OF LOW CARBON STEELS WITH AL AND SI FOR ELECTRICAL APPLICATIONS

Autoria

Silva, Thaisa Franco

Silva, Thaisa Franco

Eu sou esse autor

DOI

10.5151/2594-5300-39619

Downloads

Resumo

NESTE TRABALHO SERÁ APRESENTADA A MELHORIA DO DESEMPENHO OPERACIONAL E DA QUALIDADE EM PLACAS DE BAIXO CARBONO LIGADOS AO AL E SI PARA APLICAÇÕES ELÉTRICAS. ATRAVÉS DO CONTROLE DE VARIÁVEIS DE PROCESSO E DE FERRAMENTAS ESTATÍSTICAS, FOI POSSÍVEL IDENTIFICAR UM AÇO ESPECÍFICO NOS AÇOS DE BAIXO CARBONO QUE APRESENTA ALTO ÍNDICE DE ALARMES DE COLAMENTO QUANDO COMPARADO AOS AÇOS DE BAIXO CARBONO CONVENCIONAIS. ALÉM DISSO, ESTES ALARMES CAUSAM QUEDAS EM ALGUMAS PLACAS E EVENTUALMENTE INTERRUPÇÃO DA SEQUÊNCIA. ANALISANDO A COMPOSIÇÃO QUÍMICA DO AÇO E A MODIFICAÇÃO DA COMPOSIÇÃO QUÍMICA DO FLUXANTE DURANTE O LINGOTAMENTO, ATRAVÉS DA AMOSTRAGEM DO FLUXANTE NO MOLDE, E FOI POSSÍVEL IDENTIFICAR A RAZÃO DOS PROBLEMAS OPERACIONAIS E DE QUALIDADE, QUE ESTÃO RELACIONADOS AO PICK UP DE AL2O3 DO FLUXANTE NO MOLDE, QUE LEVA AO AUMENTO DA VISCOSIDADE E LUBRIFICAÇÃO DEFICIENTE. UM FLUXANTE ESPECÍFICO FOI SUGERIDO E TESTADO PARA MANTER A CAPACIDADE DE LUBRIFICAÇÃO MESMO COM ALTA CAPTAÇÃO DE AL2O3. FOI POSSÍVEL MEDIR A MELHORIA ATRAVÉS DO ÍNDICE DE ALARMES DE COLAMENTO E FRICÇÃO NO MOLDE. AMBAS AS VARIÁVEIS APRESENTARAM MELHORIAS SIGNIFICATIVAS, QUE LEVAM A MELHOR QUALIDADE E RESULTADOS OPERACIONAIS.

In this paper will be presented the improvement of operational and quality performance in slabs of low carbon Al and Si alloyed for electrical applications. Using the process variables controlling and statistical tools, it was possible to identify a specific steel into the low carbon steel grades which presented high breakout alarms index when compared to conventional low carbon grades. In addition, these alarms caused downgrades in some slabs and eventually heat sequence interruption. Analyzing the steel chemical composition and the flux chemical composition modification during the casting, by sampling the liquid mold flux, it was possible to identify the reason of operational and quality problems, that is related to Al2O3 mold flux pick up, that leads to viscosity increase and deficient lubrication. A specific mold flux was suggested and tested to maintain the lubrication capacity even with high Al2O3 mold flux pick up. It was possible to measure the improvement using the breakout alarms index and the friction in the mold. Both variables presented significative improvement, which lead to better quality and operational results.

Palavras-chave

lINGOTAMENTO CONTÍNUO; AÇOS ELÉTRICOS; FLUXANTE

Continuous Casting; Electrical Steels; Fluxes