Título

METODOLOGIAS DE APLICAÇÃO DE MICRODUREZA VICKERS PARA AVALIAÇÃO DA CINÉTICA DE AUSTENITIZAÇÃO INTERCRÍTICA EM UM AÇO TRIP 780

VICKERS MICROHARDNESS APPLICATION TO ASSESS INTERCRITICAL AUSTENITIZING KINETICS IN A TRIP 780 STEEL

Autoria

SILVA, EDUARDO ANTONIO LAIA DA; FARIA, GERALDO LÚCIO DE

SILVA, EDUARDO ANTONIO LAIA DA

Eu sou esse autor

FARIA, GERALDO LÚCIO DE

Eu sou esse autor

DOI

10.5151/2594-5327-40520

Downloads

Resumo

DEVIDO àS DIVERSAS DEMANDAS DA INDúSTRIA AUTOMOTIVA, A TERCEIRA GERAçãO DE AçOS ADVANCED HIGH STRENGTH STEEL (AHSS) TEM SIDO DESENVOLVIDA. ALGUNS PROCESSOS, COMO O DE TêMPERA E PARTIçãO (QUENCHING AND PARTITIONING – Q&P), TêM SIDO PROPOSTOS PARA MELHORAR AS PROPRIEDADES MECâNICAS DESSES AçOS, VISANDO APLICAçõES ESPECíFICAS. PARA AUMENTAR O POTENCIAL DE APLICAçãO DESTE TRATAMENTO TéRMICO, UMA ROTA ANTERIOR AO PROCESSO DE Q&P DENOMINADA AUSTENITIZAçãO INTERCRíTICA (INTERCRITICAL AUSTENITIZING – IA) TEM SIDO APLICADA. CONTUDO, PEQUENAS VARIAçõES EM IMPORTANTES PARâMETROS DE PROCESSAMENTO, COMO A TAXA DE AQUECIMENTO, CAUSAM SIGNIFICATIVAS ALTERAçõES NA EVOLUçãO MICROESTRUTURAL E PODEM COMPROMETER O RESULTADO FINAL DO CICLO TéRMICO. PARA QUE HAJA O MíNIMO DE DIVERGêNCIAS QUANTO àS PREVISõES DOS RESULTADOS ALCANçADOS EM FUNçãO DO CICLO TéRMICO EXPERIMENTALMENTE APLICADO, MODELOS DE PREVISãO TêM SIDO AMPLAMENTE UTILIZADOS. NESTE CONTEXTO, O PRESENTE TRABALHO PROPõE DOIS MéTODOS DE APLICAçãO DA MICRODUREZA VICKERS (VICKERS MICROHARDNESS – HV) COMO FERRAMENTAS DE PREVISIBILIDADE DA FRAçãO DE FASES PRESENTES NA MICROESTRUTURA DO AçO ESTUDADO QUANDO INTERCRITICAMENTE AUSTENITIZADO.

DUE TO VARIED DEMANDS FROM THE AUTOMOTIVE INDUSTRY, THE THIRD GENERATION OF ADVANCED HIGH STRENGTH STEEL (AHSS) HAS BEEN DEVELOPED. SOME PROCESSES, SUCH AS QUENCHING AND PARTITIONING (Q&P), HAVE ALSO BEEN PROPOSED TO IMPROVE THE MECHANICAL PROPERTIES OF THESE STEELS, TARGETING SPECIFIC APPLICATIONS. TO INCREASE THE APPLICATION POTENTIAL OF THIS HEAT TREATMENT, A ROUTE PRIOR TO THE Q&P PROCESS NAMED INTERCRITICAL AUSTENITIZING (IA) HAS BEEN APPLIED. HOWEVER, SMALL VARIATIONS IN IMPORTANT PROCESSING PARAMETERS, SUCH AS THE HEATING RATE, CAUSE SIGNIFICANT CHANGES IN THE MICROSTRUCTURAL EVOLUTION AND CAN COMPROMISE THE FINAL RESULT OF THE THERMAL CYCLE. TO ENSURE THAT THERE IS A MINIMUM OF DIVERGENCES ON THE PREDICTION OF RESULTS DEPENDING ON THE EXPERIMENTALLY APPLIED THERMAL CYCLE, PREDICTION MODELS HAVE BEEN WIDELY USED. IN THIS CONTEXT, THE PRESENT WORK PROPOSES TWO METHODS OF APPLYING VICKERS MICROHARDNESS (HV) AS TOOLS FOR PREDICTING THE FRACTION OF PHASES PRESENT IN THE MICROSTRUCTURE OF THE STUDIED STEEL WHEN INTERCRITICALLY AUSTENITIZED.

Palavras-chave

Austenitização Intercrítica; Microdureza Vickers; Aço TRIP 780; Modelo de Previsibilidade

Intercritical Austenitizing; Vickers Microhardness; TRIP 780 Steel; Previsibility Modelling.