PROPRIEDADES DO ESTADO ENDURECIDO DE ARGAMASSAS COM INCORPORAÇÃO DE RESÍDUO DE PLACAS DE GESSO

PROPERTIES OF THE HARD STATE OF MORTARS WITH INCORPORATION OF PLASTER PLATE WASTE

Autoria

Marvila, Markssuel Teixeira; Azevedo, Afonso Rangel Garcez de; Delaqua, Geovana Carla Girondi; Zanelato, Euzébio Bernabé; Barbosa, Victor de Souza; Lima, Thuany Espirito Santo; Monteiro, Sergio Neves; Xavier, Gustavo Castro; Alexandre, Jonas; Vieira, Carlos Maurício Fontes

DOI

10.5151/2594-5327-34039

Downloads

Baixar Artigo 11 Downloads

Resumo

OS RESÍDUOS DA CONSTRUÇÃO CIVIL SÃO PROBLEMÁTICOS DEVIDO A SUA CARACTERÍSTICA HETEROGÊNEA, A GRANDE QUANTIDADE GERADA E A FALTA DE METODOLOGIAS DE RECICLAGEM. ASSIM, O OBJETIVO DESSE TRABALHO FOI UTILIZAR RESÍDUO DE PLACA DE GESSO DE CONSTRUÇÃO CIVIL EM ARGAMASSAS COMO SUBSTITUTO DE AREIA EM PROPORÇÕES DE 0%, 20%, 40% E 60%, UTILIZANDO UMA ARGAMASSA 1:1:6:1,5 (CIMENTO: CAL HIDRATADA: AREIA: ÁGUA), E REALIZANDO ENSAIOS DO ESTADO ENDURECIDO DE ARGAMASSAS, TAIS COMO RESISTÊNCIA À TRAÇÃO NA FLEXÃO, RESISTÊNCIA À COMPRESSÃO, DENSIDADE DE MASSA NO ESTADO ENDURECIDO, ABSORÇÃO DE ÁGUA E ÍNDICE DE VAZIOS. OS RESULTADOS COMPROVAM A VIABILIDADE DA UTILIZAÇÃO DE 20% DO RESÍDUO DE PLACA DE GESSO, UMA VEZ QUE COM ESSA PORCENTAGEM O MATERIAL ATUA COMO PREENCHIMENTO DE VAZIOS, MELHORANDO AS PROPRIEDADES DE RESISTÊNCIA À COMPRESSÃO, POR EXEMPLO. TEORES DE 40% E 60% SÃO INVIÁVEIS DEVIDO A AGLOMERAÇÃO DO RESÍDUO DENTRO DA MATRIZ CIMENTÍCIA, POR ISSO CONCLUI-SE QUE PARA RECICLAGEM DO RESÍDUO SEM PREJUDICAR AS PROPRIEDADES DA ARGAMASSA DEVE-SE UTILIZAR 20% DE SUBSTITUIÇÃO DA AREIA POR RESÍDUO DE PLACA DE GESSO

 

CONSTRUCTION WASTE IS PROBLEMATIC DUE TO ITS HETEROGENEOUS CHARACTERISTIC, THE LARGE AMOUNT GENERATED AND THE LACK OF RECYCLING METHODOLOGIES. THUS, THE OBJECTIVE OF THIS WORK WAS TO USE PLASTER PLATE RESIDUE FROM MORTAR AS A SUBSTITUTE FOR SAND IN PROPORTIONS OF 0%, 20%, 40% AND 60%, USING A MORTAR 1: 1: 6: 1.5 ( CEMENT: HYDRATED LIME: SAND: WATER), AND CARRYING OUT TESTS OF THE HARDENED STATE OF MORTAR, SUCH AS FLEXURAL TENSILE STRENGTH, COMPRESSIVE STRENGTH, MASS DENSITY IN THE HARDENED STATE, WATER ABSORPTION AND VOIDS INDEX. THE RESULTS PROVE THE FEASIBILITY OF USING 20% OF THE PLASTER PLATE RESIDUE, SINCE WITH THIS PERCENTAGE THE MATERIAL ACTS AS FILLING IN VOIDS, IMPROVING THE PROPERTIES OF COMPRESSIVE STRENGTH, FOR EXAMPLE. LEVELS OF 40% AND 60% ARE NOT VIABLE DUE TO THE AGGLOMERATION OF THE RESIDUE WITHIN THE CEMENTITIOUS MATRIX, WHICH IS WHY IT IS CONCLUDED THAT FOR RECYCLING THE RESIDUE WITHOUT IMPAIRING THE PROPERTIES OF THE MORTAR, 20% REPLACEMENT OF SAND BY PLASTER PLATE RESIDUE SHOULD BE USED