RESÍDUO DE VIDRO UTILIZADO EM SUBSTITUIÇÃO À AREIA EM UMA MASSA CERÂMICA

GLASS WASTE USED TO REPLACE SAND IN CERAMIC MASS

Autoria

DELAQUA, GEOVANA CARLA GIRONDI; SOUZA, DJALMA; VIEIRA, CARLOS MAURÍCIO FONTES

DELAQUA, GEOVANA CARLA GIRONDI

Eu sou esse autor

SOUZA, DJALMA

Eu sou esse autor

VIEIRA, CARLOS MAURÍCIO FONTES

Eu sou esse autor

DOI

10.5151/2594-5327-41281

Downloads

Resumo

TRABALHO TEM POR OBJETIVO AVALIAR A INFLUêNCIA DA SUBSTITUIçãO DA AREIA POR RESíDUO DE VIDRO NAS PROPRIEDADES FíSICAS E MECâNICAS DE UMA COMPOSIçãO TíPICA DE CERâMICA VERMELHA. O RESíDUO é PROVENIENTE DA PRIMEIRA ETAPA DE FABRICAçãO DE VIDROS EM UM PROCESSO CONVENCIONAL DE TêMPERA. CORPOS DE PROVA CERâMICOS FORAM PREPARADOS COM INCORPORAçõES DE 0, 10 E 20% DE RESíDUO. AS AMOSTRAS FORAM OBTIDAS POR EXTRUSãO, SECAS E QUEIMADAS EM 800 E 900°C EM FORNO DE LABORATóRIO. FORAM REALIZADAS ANáLISES DAS MATéRIAS-PRIMAS, DENTRE AS QUAIS SE PODEM DESTACAR AS FíSICAS E QUíMICAS, E POSTERIORMENTE FORAM REALIZADOS TESTES NAS PEçAS CERâMICAS QUEIMADAS. AS PROPRIEDADES OBTIDAS DE QUEIMA FORAM A ABSORçãO DE áGUA, RETRAçãO LINEAR DE QUEIMA E TENSãO DE RUPTURA à FLEXãO. OS RESULTADOS OBTIDOS DEMONSTRARAM QUE TANTO O AUMENTO DO TEOR DE VIDRO QUANTO O AUMENTO DA TEMPERATURA INFLUENCIARAM POSITIVAMENTE NAS PROPRIEDADES ESTUDADAS, E, ALéM DISSO, O VIDRO ATUOU DE MODO A REDUZIR A TEMPERATURA ADEQUADA DE QUEIMA

THE AIM OF THE WORK IS TO EVALUATE THE INFLUENCE OF REPLACING SAND WITH GLASS WASTE ON THE PHYSICAL AND MECHANICAL PROPERTIES OF A TYPICAL RED CERAMIC COMPOSITION. THE RESIDUE COMES FROM THE FIRST STAGE OF GLASS MANUFACTURING IN A CONVENTIONAL TEMPERING PROCESS. CERAMIC SPECIMENS WERE PREPARED WITH INCORPORATIONS OF 0, 10 AND 20% OF WASTE. THE SAMPLES WERE OBTAINED BY EXTRUSION, DRIED AND FIRED AT 800 AND 900°C IN A LABORATORY OVEN. ANALYZES OF THE RAW MATERIALS WERE CARRIED OUT, INCLUDING PHYSICAL AND CHEMICAL ONES, AND TESTS WERE SUBSEQUENTLY CARRIED OUT ON FIRED CERAMIC PIECES. THE PROPERTIES OBTAINED FROM FIRING WERE WATER ABSORPTION, LINEAR FIRING SHRINKAGE AND FLEXURAL RUPTURE STRENGTH. THE RESULTS OBTAINED DEMONSTRATED THAT BOTH THE INCREASE IN GLASS CONTENT AND THE INCREASE IN TEMPERATURE HAD A POSITIVE INFLUENCE ON THE PROPERTIES STUDIED, AND, IN ADDITION, THE GLASS ACTED TO REDUCE THE APPROPRIATE FIRING TEMPERATURE