REVESTIMENTOS CERÃMICOS SEMIPOROSOS OBTIDOS COM ADIÇÃO DE FONOLITOS EM MASSAS ARGILOSAS CAULINÍTICAS

SEMIPOROUS CERAMIC COATINGS OBTAINED WITH ADDITION OF PHONOLITES IN CAULINIQUE ARGYLUS PASTS

DOI

10.5151/1516-392X-30806

Downloads

Baixar Artigo 233 Downloads

Resumo

Este trabalho tem por objetivo avaliar a possibilidade de obtenção de revestimento cerâmico prensado semiporoso utilizando misturas, por via seca, de argila caolinítica com fonolíto. Foram utilizados traços contendo 20% e 40% de incorporação de fonolíto em peso em relação a massa cerâmica em duas granulometrias distintas (fonolíto passado na peneira #50 e #200). Para efeito comparativo, avaliou-se uma massa cerâmica industrial proveniente do polo cerâmico de Campos dos Goytacazes e uma massa cerâmica sem incorporação de fonolíto. Foram preparados corpos de prova por prensagem uniaxial calcinados em temperaturas variando entre 1050 a 1200º C. Nas amostras queimadas, foram realizados ensaios tecnológicos para determinação da retração linear, resistência mecânica (compressão diametral) e absorção de água. Os resultados mostraram que a adição de fonolíto reduziu a absorção de água da argila. Além disso, o incremento do teor de fonolíto e a redução de sua granulometria somente foram eficientes em temperaturas elevadas. Com isso, a incorporação de fonolíto a uma argila caolinítica pode possibilitar a obtenção de revestimentos semiporosos com parâmetros melhorados. Entretanto uma ressalva dever ser feita: há necessidade de incremento da temperatura final de queima em comparação com patamares utilizados por indústrias do polo cerâmico de Campos dos Goytacazes.

 

This work aims to evaluate the possibility of obtaining a semiporous pressed ceramic coating using dry mixtures of kaolinite clay with phonolite. Traces containing 20% and 40% of fonolite incorporation by weight in relation to the ceramic mass were used in two distinct granulometries (phonolite passed in the # 50 and # 200 sieves). For comparative purposes, an industrial ceramic mass was obtained from the Campos dos Goytacazes ceramic pole and a ceramic mass without incorporation of fonolíto. Uniaxial pressing specimens calcined at temperatures ranging from 1050 to 1200 ° C were prepared. In the burned samples, technological tests were carried out to determine linear retraction, mechanical strength (diametrical compression) and water absorption. The results showed that the addition of phonolite reduced the water absorption of the clay. In addition, the increase of the phonolite content and the reduction of its granulometry were only efficient at high temperatures. Thus, the incorporation of phonolite into a kaolinitic clay can make it possible to obtain semiporous coatings with improved parameters. However, a caveat must be made: there is a need to increase the final firing temperature in comparison to the levels used by the Campos dos Goytacazes.

Palavras-chave

Argila caolinítica, Fonolíto, Revestimento Cerâmico Semiporoso

Clay kaolinite, Fonolite, Semi Porous Ceramic Flooring.

Como citar

Marvila, Markssuel Teixeira; Alexandre, Jonas; Azevedo, Afonso Rangel Garcez; Zanelato, Euzebio Bernabé; Monteiro, Sergio Neves; Xavier, Gustavo Castro; Rangel, Greisson Peixoto. REVESTIMENTOS CERÃMICOS SEMIPOROSOS OBTIDOS COM ADIÇÃO DE FONOLITOS EM MASSAS ARGILOSAS CAULINÍTICAS , p. 2979-2986. In: 72nd ABM Annual Congress, São Paulo, 2017.