SINTERIZAÇÃO POR ALTA PRESSÃO DE COMPÓSITO DE METAL DURO A PARTIR DE PÓS ULTRAFINOS: ESTRUTURA, MICROESTRUTURA E PROPRIEDADES MECÂNICAS: HIGH PRESSURE AIDED SINTERING OF ULTRAFINE POWDERS OF WC HARDMETALS: STRUCTURE, MICROSTRUCTURE AND MECHANICAL PROPERTIES

Borges, Lidiane Hott de Fúcio; Oliveira, Hellen Cristina Prata de; Guimarães, Renan da Silva; Quintanilha, Ronaldo; Crespo, Alexsandre da Silva; Filgueira, Marcello

doi:10.5151/2594-5327-0079

Anais do Congresso Anual da ABM

ISSN 2594-5327

63º Congresso Anual da ABM — vol. 63, num.63 (2008)

Título

SINTERIZAÇÃO POR ALTA PRESSÃO DE COMPÓSITO DE METAL DURO A PARTIR DE PÓS ULTRAFINOS: ESTRUTURA, MICROESTRUTURA E PROPRIEDADES MECÂNICAS

HIGH PRESSURE AIDED SINTERING OF ULTRAFINE POWDERS OF WC HARDMETALS: STRUCTURE, MICROSTRUCTURE AND MECHANICAL PROPERTIES

Autoria

Borges, Lidiane Hott de Fúcio; Oliveira, Hellen Cristina Prata de; Guimarães, Renan da Silva; Quintanilha, Ronaldo; Crespo, Alexsandre da Silva; Filgueira, Marcello

Oliveira, Hellen Cristina Prata de

Eu sou esse autor

10.5151/2594-5327-0079

Downloads

Baixar Artigo 91 Downloads

Resumo

As ligas de metal duro são processadas via sinterização por fase líquida, as quais consistem de um carbeto refratário, embebido numa matriz tenaz de cobalto. Estas ligas são extensivamente utilizadas em aplicações que demandam resistência a abrasão e alta dureza. O presente trabalho tem como objetivo analisar a sinterização de pós ultrafinos de carbeto de tungstênio (WC) com a adição de 10%pesoCo. As ligas foram processadas pela técnica das altas pressões e altas temperaturas. Foi estudada a sinterização da liga WC/10%pCo a 3, 4 e 5 GPa, nas temperaturas de 1300,1400 e 1500oC, para os tempos de 2 e 4 minutos. As análises foram feitas por microscopia eletrônica de varredura, densificação, difração de raios-X, dureza Vickers e tenacidade à fratura. Os melhores resultados obtidos foram: densidade =98,9%, dureza HV30 =10,77 GPa e tenacidade à fratura KIC = 15,57 MPam

Hardmetal alloys are processed by liquid phase sintering, which consist of one refractory carbide, embebided in to a tough matrix of Co. These alloys extensively are used in applications that demand abrasion resistance and high hardness. The present work has as objective to analyze the sintering of ultrafine powders of tungsten carbide (WC) with the addition of 10%wtCo. The alloys had been prepared by using high pressure and high temperature technique. The sintering of the WC/10%pCo alloy was processed at the 3, 4 and 5 GPa, in temperatures of 1300,1400 and 1500oC, during 2 and 4 minutes. The analysis was made by microstructure, densification, structure, Vickers hardness and fracture toughness. The best results was density = 98.9%, hardness HV30 =10,77GPa and fracture toughness 1/2 KIC = 15,57 MPa.m .

Palavras-chave

Sinterização HPHT; Metal duro ultrafino; Dureza; Tenacidade à fratura.

HPHT Sintering, Ultrafine Hardmetal, Hardness, Fracture Toughness.

Como citar

Borges, Lidiane Hott de Fúcio; Oliveira, Hellen Cristina Prata de; Guimarães, Renan da Silva; Quintanilha, Ronaldo; Crespo, Alexsandre da Silva; Filgueira, Marcello. SINTERIZAÇÃO POR ALTA PRESSÃO DE COMPÓSITO DE METAL DURO A PARTIR DE PÓS ULTRAFINOS: ESTRUTURA, MICROESTRUTURA E PROPRIEDADES MECÂNICAS , p. 726-732. In: 63º Congresso Anual da ABM, Santos - SP, 2008.