Título

SOLDAGEM DE REVESTIMENTO COM INCONEL 625 EM AÇO SAE 4140 UTILIZANDO LASER CLADDING

COATING WELDING OF INCONEL 625 IN SAE 4140 USING LASER CLADDING

Autoria

Mougo, Adriane Lopes; Senne, Bernardo Alves de; Ornellas, Daniel Soares Portela de; Oliveira, Kaique do Rosário

Mougo, Adriane Lopes

Eu sou esse autor

Senne, Bernardo Alves de

1 Artigos, Baixados 11 Vezes

Ornellas, Daniel Soares Portela de

Eu sou esse autor

Oliveira, Kaique do Rosário

Eu sou esse autor

DOI

10.5151/2594-5327-34672

Downloads

Resumo

ESTE TRABALHO TEM COMO OBJETIVO ANALISAR E COMPARAR AS CARACTERÍSTICAS METALÚRGICAS E GEOMÉTRICAS DE UMA SOLDAGEM DE REVESTIMENTO PELO PROCESSO LASER CLADDING UTILIZANDO COMO METAL DE ADIÇÃO A SUPERLIGA DE NÍQUEL INCONEL 625 SOBRE AÇO MÉDIO CARBONO AISI/SAE 4140. AS SOLDAS FORAM APLICADAS NA FORMA DE REVESTIMENTO E OS PARÂMETROS DE ENTRADA FORAM A POTÊNCIA E A VELOCIDADE DE SOLDAGEM. UTILIZANDO A ANOVA FOI VISTO QUE A VELOCIDADE EXERCE INFLUÊNCIA RELEVANTE SOBRE A LARGURA E ALTURA DO CORDÃO ISOLADO E SOBRE A ALTURA DO REVESTIMENTO, ENQUANTO A ZTA DO CORDÃO ISOLADO SOFRE MAIS INFLUÊNCIA DA POTÊNCIA. A LINHA DE FUSÃO APRESENTOU ZPMS (ZONAS PARCIALMENTE MISTURADAS). AS MICRODUREZAS MENSURADAS NESSAS REGIÕES APONTARAM 612 HV E 517 HV, RESPECTIVAMENTE, CONFIRMANDO A FORMAÇÃO DE MARTENSITA. AS MICRODUREZAS DO METAL DE BASE E METAL DE ADIÇÃO DE TODAS AS AMOSTRAS APRESENTARAM RESULTADOS HOMOGÊNEOS COM 250 HV DE DUREZA MÉDIA, ENQUANTO A ZTA SOFREU VARIAÇÃO BRUSCA. NO GERAL, OBSERVA-SE QUE AS AMOSTRAS SOLDADAS COM A MENOR VELOCIDADE (8 MM/S), APRESENTARAM MENORES MÉDIAS DE MICRODUREZA DA ZTA.

THE PRESENT PAPER AIMS TO EVALUATE AND COMPARE THE METALLURGICAL AND GEOMETRIC ASPECTS OF A OVERLAY WELDING USING THE LASER CLADDING PROCESS WITH NICKEL BASE SUPERALLOY INCONEL 625 AS FILLER METAL ON BASE METAL AISI/SAE 4140. THE WELDS WERE APPLIED AS COATINGS. THE INPUT PARAMETERS WERE THE LASER POWER AND SCANNING SPEED. USING ANOVA, IT WAS OBSERVED THAT THE SPEED HAS A RELEVANT INFLUENCE ON THE WIDTH AND HEIGHT OF THE SINGLE BEAD AND ALSO ON THE HEIGHT OF THE OVERLAPPED BEADS, WHILE THE HAZ OF THE SINGLE BEAD SUFFERED MORE INFLUENCE OF THE LASER POWER. THE FUSION LINE SHOWED PMZS (PARTIAL MIXED ZONES). THE MICROHARDNESS VALUES MEASURED IN THESE AREAS POINTED 612 HV AND 517 HV, RESPECTIVELY, CONFIRMING THE FORMATION OF MARTENSITE. THE MICROHARDNESS OF BOTH BASE METAL AND FILLER METAL OF ALL SAMPLES PRESENTED HOMOGENEOUS RESULTS WITH 250 HV OF MEDIUM HARDNESS, WHILE THE HAZ SUFFERED LARGE VARIATION. IN GENERAL, IT IS OBSERVED THAT THE SAMPLES WELDED WITH THE LOWEST SPEED (8 MM/S), PRESENTED LOWER AVERAGES OF HAZ MICROHARDNESS.

Palavras-chave

Laser Cladding; Microdureza; Aspectos Geométricos

Laser Cladding; Microhardness; Geometric Aspects.