TRABALHO DE ALÍVIO DE TENSÃO EM UMA LÂMIDA DESGASTADA DE AÇO CROMO VANÁDIO

TENSION RELIEF WORK ON AN UNPLUGGED STEEL BLADE CHROMO VANÁDIO

Autoria

Cunha, Dayllan Alves; Tardim, João Lucas Moreira; Souzar, Victor Barbosa de; Silva, Júlia de Mello; Lima, Amanda Camerini; Azevedo, Afonso Rangel Garcez de; Marvila, Markssuel Teixeira; Monteiro, Sergio Neves; Zanelato, Euzébio Bernabe

DOI

10.5151/2594-5327-34049

Downloads

Baixar Artigo 11 Downloads

Resumo

A LÂMINA DE ROÇADEIRA É UM EQUIPAMENTO ESSENCIAL PARA O CORTE DE VEGETAÇÃO, QUE CONSISTE NA RETIRADA DO EXCESSO DE GRAMA. ESTA LÂMINA É COMPOSTA DE UM AÇO ESPECIAL QUE LHE CONCEDE ALTA DUREZA, RESISTÊNCIA À CORROSÃO, RESISTÊNCIA À ABRASÃO E LHE CONFERE UMA MAIOR TEMPERABILIDADE, ESSE AÇO É O AÇO CROMO VANÁDIO. OS ENSAIOS REALIZADOS NESTE TRABALHO TÊM COMO OBJETIVO VERIFICAR COMO UMA LÂMINA DE AÇO CROMO VANÁDIO JÁ TENDO HORAS DE TRABALHO, QUE LHE CONFEREM UMA CARACTERÍSTICA DE ALTA DUREZA (PELA AÇÃO DO AQUECIMENTO E RESFRIAMENTO PARA AFIÁ-LA) SE COMPORTA EM UM ENSAIO DE DUREZA SE COMPARADA A UMA LÂMINA NOVA. POSTERIORMENTE A ESTÁ COMPARAÇÃO FOI REALIZADO UM TRATAMENTO TÉRMICO DE RECOZIMENTO, COM INTUITO DE RECUPERAR AS CARACTERÍSTICAS DE FÁBRICA DO MATERIAL E NOVAMENTE SER COMPARADA COM UMA LÂMINA NOVA. O RECOZIMENTO FOI FEITO EM FORNO INDUSTRIAL A UMA TEMPERATURA NA FAIXA DE 800°C DURANTE O PERÍODO DE 3 HORAS E POSTERIORMENTE RESFRIADA DENTRO DO MESMO FORNO, APÓS O PROCESSO FOI FEITO UMA ANÁLISE DE DUREZA. O PROCESSO DE RECOZIMENTO FEZ COM QUE A LÂMINA USADA TIVESSE UMA REDUÇÃO SIGNIFICATIVA DE SUA DUREZA, DIMINUINDO ASSIM A CHANCE DE SUA FRATURA E ALCANÇANDO CARACTERÍSTICAS DE UMA LÂMINA NOVA

 

THE BRUSH CUTTER BLADE IS AN ESSENTIAL EQUIPMENT FOR CUTTING VEGETATION, WHICH CONSISTS OF REMOVING EXCESS GRASS. THIS BLADE IS COMPOSED OF A SPECIAL STEEL THAT GIVES IT HIGH HARDNESS, RESISTANCE TO CORROSION, RESISTANCE TO ABRASION AND GIVES IT GREATER TEMPERABILITY, THIS STEEL IS CHROME VANADIUM STEEL. THE TESTS CARRIED OUT IN THIS WORK AIM TO VERIFY HOW A CHROME VANADIUM STEEL BLADE ALREADY HAS HOURS OF WORK, WHICH GIVE IT A HIGH HARDNESS CHARACTERISTIC (BY HEATING AND COOLING TO SHARPEN IT) BEHAVES IN A HARDNESS TEST IF COMPARED TO A NEW BLADE. SUBSEQUENTLY TO THIS COMPARISON, AN ANNEALING HEAT TREATMENT WAS CARRIED OUT IN ORDER TO RECOVER THE MATERIAL'S FACTORY CHARACTERISTICS AND AGAIN BE COMPARED WITH A NEW BLADE. ANNEALING WAS CARRIED OUT IN AN INDUSTRIAL OVEN AT A TEMPERATURE IN THE RANGE OF 800 ° C FOR A PERIOD OF 3 HOURS AND THEN COOLED INSIDE THE SAME OVEN, AFTER THE PROCESS A HARDNESS ANALYSIS WAS CARRIED OUT. THE ANNEALING PROCESS MEANT THAT THE USED BLADE HAD A SIGNIFICANT REDUCTION IN ITS HARDNESS, THUS DECREASING THE CHANCE OF FRACTURE AND ACHIEVING CHARACTERISTICS OF A NEW BLADE.

Palavras-chave

Lâmina; Roçadeira; Aço cromo vanádio; Recozimento

Blade; Brush cutter; Chrome vanadium steel; Annealing