TRATAMENTOS ALCALINOS EM FIBRAS NATURAIS DA PALHA DE MILHO APLICADO EM COMPÓSITOS CIMENTÍCIOS: ALKALINE TREATMENTS ON NATURAL CORN STRAW FIBERS APPLIED IN CEMENTIOUS COMPOSITES

DEVIDO AO GRANDE POTENCIAL DE SUBSTITUIçãO DE FIBRAS SINTéTICAS POR FIBRAS NATURAIS, DIVERSOS ESTUDOS TêM SIDO REALIZADOS OBJETIVANDO CONCILIAR O CRESCIMENTO DA INDúSTRIA DA CONSTRUçãO COM O DESENVOLVIMENTO SUSTENTáVEL. DIANTE DISSO, O OBJETIVO DESTA PESQUISA FOI COMPARAR TRêS DIFERENTES TRATAMENTOS ALCALINOS EM FIBRA DE PALHA DE MILHO INCORPORADA EM ARGAMASSAS DE CIMENTO E CAL PARA APLICAçãO EM REVESTIMENTO E ASSENTAMENTO DE PAREDES E TETOS. CORPOS DE PROVA CILíNDRICOS COM DIMENSõES 50X100 MM FORAM CONFECCIONADOS UTILIZANDO 0%, 2,5% E 5% DE FIBRAS NATURAIS E FIBRAS TRATADAS COM HIDRóXIDO DE SóDIO (NAOH), HIDRóXIDO DE POTáSSIO (KOH) E HIDRóXIDO DE CáLCIO (CA(OH)2) PARA A COMPOSIçãO 1: 1:6:1,55 (CIMENTO: CAL: AREIA: áGUA). PARA O ESTADO ENDURECIDO AS MISTURAS FORAM AVALIADAS QUANTO à RESISTêNCIA à COMPRESSãO, ABSORçãO DE áGUA, DENSIDADE E POROSIDADE, E PARA O ESTADO FRESCO QUANTO à SUA CONSISTêNCIA. FORAM REALIZADAS CARACTERIZAçõES QUíMICAS, FíSICAS E MINERALóGICAS DAS FIBRAS. PARA A CARACTERIZAçãO QUíMICA DAS FIBRAS CONSTATOU-SE O AUMENTO DA CELULOSE CRISTALINA DE 59,03% PARA 63,50% (NAOH), 62,41% (KOH), 60,40% (CA(OH)2), O QUE FAVORECE A RESISTêNCIA DA FIBRA. OS RESULTADOS DE ABSORçãO DE áGUA MOSTRARAM QUE A ARGAMASSA CONTENDO AS FIBRAS TRATADAS APRESENTOU VALORES INFERIORES EM RELAçãO à FIBRA NATURAL, SENDO UM PONTO POSITIVO PARA RESISTêNCIA MECâNICA. OUTRO PONTO POSITIVO QUE OS TRATAMENTOS ALCALINOS APRESENTARAM FOI A REDUçãO DO TEOR DE IMPUREZAS DA FIBRA NATURAL, PRINCIPALMENTE O TRATAMENTO COM HIDRóXIDO DE SóDIO (NAOH), COM REDUçãO DE 4,69%. ASSIM, PODE-SE CONCLUIR QUE OS TRATAMENTOS MELHORARAM AS PROPRIEDADES DA FIBRA, VIABILIZANDO SUA UTILIZAçãO EM ARGAMASSAS PARA REVESTIMENTO E ASSENTAMENTO DE PAREDES E TETOS. VALE RESSALTAR QUE O TRATAMENTO COM HIDRóXIDO DE SóDIO (NAOH) MOSTROU-SE MAIS EFICIENTE NAS DIFERENTES PROPRIEDADES AVALIADAS

DUE TO THE GREAT POTENTIAL FOR REPLACING SYNTHETIC FIBERS WITH NATURAL FIBERS, SEVERAL STUDIES HAVE BEEN CARRIED OUT AIMING TO RECONCILE THE GROWTH OF THE CONSTRUCTION INDUSTRY WITH SUSTAINABLE DEVELOPMENT. THEREFORE, THE OBJECTIVE OF THIS RESEARCH WAS TO COMPARE THREE DIFFERENT ALKALINE TREATMENTS ON CORN STRAW FIBER INCORPORATED IN CEMENT AND LIME MORTARS FOR APPLICATION IN COVERING AND LAYING WALLS AND CEILINGS. CYLINDRICAL SPECIMENS MEASURING 50X100 MM WERE MADE USING 0%, 2.5% AND 5% NATURAL FIBERS AND FIBERS TREATED WITH SODIUM HYDROXIDE (NAOH), POTASSIUM HYDROXIDE (KOH) AND CALCIUM HYDROXIDE (CA(OH)2) FOR THE COMPOSITION 1: 1:6:1.55 (CEMENT: LIME: SAND: WATER). FOR THE HARDENED STATE, THE MIXTURES WERE EVALUATED FOR COMPRESSIVE STRENGTH, WATER ABSORPTION, DENSITY AND POROSITY, AND FOR THE FRESH STATE FOR THEIR CONSISTENCY. CHEMICAL, PHYSICAL AND MINERALOGICAL CHARACTERIZATIONS OF THE FIBERS WERE CARRIED OUT. FOR THE CHEMICAL CHARACTERIZATION OF THE FIBERS, AN INCREASE IN CRYSTALLINE CELLULOSE WAS FOUND FROM 59.03% TO 63.50% (NAOH), 62.41% (KOH), 60.40% (CA(OH)2), WHICH FAVORS FIBER RESISTANCE. THE WATER ABSORPTION RESULTS SHOWED THAT THE MORTAR CONTAINING THE TREATED FIBERS PRESENTED LOWER VALUES COMPARED TO THE NATURAL FIBER, BEING A POSITIVE POINT FOR MECHANICAL RESISTANCE. ANOTHER POSITIVE POINT THAT ALKALINE TREATMENTS PRESENTED WAS THE REDUCTION IN THE IMPURITY CONTENT OF THE NATURAL FIBER, MAINLY THE TREATMENT WITH SODIUM HYDROXIDE (NAOH), WITH A REDUCTION OF 4.69%. THUS, IT CAN BE CONCLUDED THAT THE TREATMENTS IMPROVED THE PROPERTIES OF THE FIBER, ENABLING ITS USE IN MORTARS FOR COVERING AND LAYING WALLS AND CEILINGS. IT IS WORTH MENTIONING THAT TREATMENT WITH SODIUM HYDROXIDE (NAOH) PROVED TO BE MORE EFFICIENT IN THE DIFFERENT PROPERTIES EVALUATED

Palavras-chave

fibra de palha de milho; fibra natural; tratamentos alcalinos

corn straw fiber; natural fiber; alkaline treatments.

Como citar

MARVILA, MARKSSUEL TEIXEIRA; SILVA, THIAGO RANILSON CAIXETA; AQUINO, LUIZ ARTHUR SILVA DE; MARQUES, MARÍLIA GONÇALVES; MESQUITA, LEONARDO CARVALHO; AZEVEDO, AFONSO RANGEL GARCEZ DE. TRATAMENTOS ALCALINOS EM FIBRAS NATURAIS DA PALHA DE MILHO APLICADO EM COMPÓSITOS CIMENTÍCIOS , p. 441-450. In: 77º Congresso Anual da ABM - Internacional, São Paulo, Brasil, 2024.
ISSN: 2594-5327 , DOI 10.5151/2594-5327-40523