Título

UTILIZAÇÃO DE CARBURETO DE CÁLCIO E LIGA CÁLCIO-SILÍCIO EM SUBSTITUIÇÃO AO FERRO-SÍLICO-MANGANÊS PARA DESOXIDAÇÃO E DESSULFURAÇÃO DE AÇO

USAGE OF CALCIUM CARBIDE AND CALCIUM-SILICON ALLOY IN REPLACEMENT TO SILICON-MANGANESE FOR STEEL DEOXIDATION AND DESULPHURIZATION

Autoria

Souza, Raphael Mariano de; Kill, Janacely Demonier; Renato, Lucas da Silva; Oliveira, José Roberto de

DOI

10.5151/2594-5300-34738

Downloads

Baixar Artigo 16 Downloads

Resumo

A DESOXIDAÇÃO E DESULFURAÇÃO DO AÇO SÃO PASSOS ESSENCIAIS PARA DAR AO PRODUTO FINAL AS PROPRIEDADES DESEJADAS, BEM COMO GARANTIR UM PROCESSO LIVRE DE ACIDENTES. ENTRE OS MATERIAIS UTILIZADOS PARA DESOXIDAÇÃO ALGUNS SãO À BASE DE SILÍCIO, COMO FERRO-SILICO-MANGANÊS E CARBETO DE SILÍCIO. NO ENTANTO, ESTES DESOXIDANTES PREJUDICAM O PROCESSO DE DESULFURAÇÃO. PORTANTO, O PRESENTE TRABALHO TEM O OBJETIVO DE ANALISAR OS EFEITOS DA DESOXIDAÇÃO VIA FESIMN NA DESULFURAÇÃO E PROPOR ALTERNATIVAS QUE PROPORCIONAM DESOXIDAÇÃO E DESULFURAÇÃO ADEQUADAS. ESTE ESTUDO FOI REALIZADO ATRAVÉS DA ANÁLISE TERMODINÂMICA DO EQUILÍBRIO AÇO-ESCÓRIA-ADIÇÕES EM UMA SIDERÚRGICA DE ROTA FEA-FP, USANDO SIMULAÇÕES TERMODINÂMICAS COMPUTACIONAIS NO FACTSAGE 8.0. UMA VEZ ANALISADOS TEORES DE EQUILÍBRIO DE S E O, VARIANDO AS ADIÇÕES DE FESIMN, CAC2 E CASI, CONCLUIU-SE QUE O USO DE FESIMN COMO DESOXIDANTE PREJUDICA A DESULFURAÇÃO DO AÇO. VERIFICA-SE TAMBÉM QUE É POSSÍVEL UTILIZAR CAC2 E CASI EM SUBSTITUIÇÃO AO FESIMN PARA PROMOVER MELHORIAS NA DESULFURAÇÃO E GARANTIR DESOXIDAÇÃO ADEQUADA DURANTE O VAZAMENTO DO AÇO.

 

STEEL DEOXIDATION AND DESULFURIZATION ARE ESSENTIAL STEPS TO GIVE THE FINAL PRODUCT THE DESIRED PROPERTIES, AS WELL AS ENSURING AN ACCIDENT-FREE PROCESS. AMONG THE MATERIALS USED FOR DEOXIDATION ARE SOME BASED ON SILICON, SUCH AS SILICON-MANGANESE AND SILICON CARBIDE. HOWEVER, THESE DEOXIDIZERS IMPAIR THE DESULPHIRIZATION PROCESS. THEREFORE, THE PRESENT WORK AIMS TO ANALYZE THE EFFECTS OF DEOXIDATION VIA FESIMN ON DESULPHURIZATION AND TO PROPOSE ALTERNATIVES THAT PROVIDE ADEQUATE DEOXIDATION AND DESULPHURIZATION. THIS STUDY WAS CARRIED OUT THROUGH THE THERMODYNAMIC ANALYSIS OF THE STEEL-SLAG-ADDITIONS BALANCE IN AN EAF STEEL MILL, USING COMPUTATIONAL THERMODYNAMIC SIMULATIONS ON FACTSAGE 8.0. ONCE ANALYZED DIFFERENT LEVELS OF EQUILIBRIUM S AND O CONTENTS VARYING THE ADDITIONS OF FESIMN, CAC2 AND CASI, IT WAS FOUND THAT THE USE OF FESIMN AS A DEOXIDIZER IMPAIRS THE DESULPHURIZATION OF THE STEEL. IT WAS ALSO FOUND THAT IT IS POSSIBLE TO USE CAC2 AND CASI IN PLACE OF FESIMN TO PROMOTE IMPROVEMENTS IN DESULPHURIZATION AND ENSURE ADEQUATE DEOXIDATION DURING THE STEEL TAPPING.

Palavras-chave

Termodinâmica computacional; Dessulfuração; Desoxidação; Refino secundário.

Computational thermodynamics; Desulphurization; Deoxidation; Secondary steelmaking.