Título

UTILIZAçãO DE MISTURAS INICIAIS A BASE DE CAO, FEO, SIO2, MGO, NA2O E CAF2 NA DESFOSFORAçãO DE FERRO-GUSA

UTILIZATION OF CAO, FEO, SIO2, MGO, NA2O AND CAF2 - BASED MIXTURES IN THE HOT METAL DEPHOSPHORIZATION

Autoria

Oliveira, Elsomar Biancardi Guimarães de; Zottich, Franklin de Souza; Pereira, Bruno Gonçalves; Silva, Caio Vaccari; Grillo, Felipe Fardin; Oliveira, José Roberto de

DOI

10.5151/2594-5300-34719

Downloads

Baixar Artigo 7 Downloads

Resumo

O OBJETIVO PRINCIPAL DESTE TRABALHO é ANALISAR A VIABILIDADE TéCNICA DA UTILIZAçãO DE MISTURAS DESFOSFORANTES INICIAIS à BASE DE CAO, FEO, SIO2, MGO, NA2O E CAF2, NO PROCESSO DE DESFOSFORAçãO DE FERRO-GUSA NO PRé-TRATAMENTO. COMO FONTE DE CAO FORAM UTILIZADOS CAL CONVENCIONAL E RESíDUO DE MáRMORE E, COMO FONTE DE FEO FOI UTILIZADO RESíDUO SIDERúRGICO CAREPA DE AçO. O DESENVOLVIMENTO DA COMPOSIçãO DA DESFOSFORAçãO FOI FEITO ATRAVéS DE CáLCULO TERMODINâMICO COMPUTACIONAL, COM A UTILIZAçãO DO SOFTWARE FACTSAGE 7.3, PARA DETERMINAR AS PROPRIEDADES DAS MISTURAS INICIAIS. FORAM COMPARADAS AS PROPRIEDADES TERMODINâMICAS E CINéTICAS DAS MISTURAS INICIAIS, A FIM DE AVALIAR A EFICIêNCIA DE DESFOSFORAçãO MEDIDA NOS EXPERIMENTOS EM ESCALA LABORATORIAL. UM NOVO MODELO DENOMINADO FATOR DE DESFOSFORAçãO MODIFICADO (FDEP-M) FOI DESENVOLVIDO PARA AVALIAR QUAL MISTURA INICIAL PODERIA SER MAIS EFICIENTE, BASEADO SOBRE SUAS PROPRIEDADES. O FDEP-M CALCULA A EFICIêNCIA DE DESFOSFORAçãO DA COMPOSIçãO QUíMICA DAS MISTURAS INICIAIS. A MISTURA DESFOSFORANTE INICIAL CONTENDO RESíDUO DE MáRMORE COM O FUNDENTE NA2O OBTEVE MELHOR EFICIêNCIA DO QUE AS DEMAIS VARIAçõES. OS RESULTADOS INDICAM A POSSIBILIDADE DE UTILIZAçãO DO RESíDUO DE MáRMORE E CAREPA COMO AGENTES DESFOSFORANTES NO PROCESSO DE DESFOSFORAçãO DE FERRO-GUSA.

 

THE MAIN OBJECTIVE OF THIS PAPER IS TO ANALYZE TECHNICAL FEASIBILITY OF UTILIZATION INITIAL DEPHOSPHORATING MIXTURES BASED ON CAO, FEO, SIO2, MGO, NA2O AND CAF2, IN THE DEPHOSPHORIZATION OF HOT METAL PRETREATMENT PROCESS. AS A SOURCE OF CAO WAS USED CONVENTIONAL LIME AND MARBLE WASTE AND, AS A SOURCE OF FEO WAS USED SCALE STEEL WASTE. THE DEVELOPMENT OF THE COMPOSITION OF THE DEPHOSPHORIZATION WAS MADE THROUGH OF COMPUTATIONAL THERMODYNAMIC CALCULATION, WITH THE UTILIZATION OF THE SOFTWARE FACTSAGE 7.3 TO DETERMINE INITIAL MIXTURES PROPERTIES. THE THERMODYNAMIC AND KINETICS OF THE INITIAL MIXTURES PROPERTIES WERE COMPARED, IN ORDER TO EVALUATE THE MEASURED DEPHOSPHORIZATION EFFICIENCY, IN THE LABORATORY SCALE EXPERIMENTS. A NEW MODEL NAMED MODIFIED DEPHOSPHORATION FACTOR (FDEP-M) WAS DEVELOPED TO EVALUATE WHICH INITIAL MIXTURE COULD BE THE MOST EFFICIENT, BASED ON ITS PROPERTIES. THE FDEP-M CALCULATES THE DEPHOSPHORIZATION EFFICIENCY OF THE CHEMICAL COMPOSITION OF THE INITIAL MIXTURES. THE INITIAL DEPHOSPHORATING MIXTURE CONTAINING MARBLE WASTE WITH FLUX NA2O ACHIEVED BETTER EFFICIENCY THAN THE OTHER VARIATIONS. THE RESULTS INDICATE THE POSSIBILITY TO USE THE MARBLE WASTE AND SCALE AS DEPHOSPHORATING AGENTS IN THE HOT METAL DEPHOSPHORIZATION PROCESS.

Palavras-chave

misturas desfosforantes; desfosforação; pré-tratamento de ferro-gusa

Dephosphorating Mixtures; Dephosphorization; Hot Metal Pretreatment