ADEQUAÇÃO DA COMPOSIÇÃO QUÍMICA DA ESCÓRIA DE ACIARIA LD PARA A FABRICAÇÃO DE CIMENTO PORTLAND

RECOVERY OF WASTE CUTTING OF GRANITE AND STEEL WORKS SCORES FROM LD FOR PRODUCTION OF PORTLAND CEMENT

Authorship

Junior, Luiz Alberto Baptista Pinto; Grillo, Felipe Fardin; Arrivabene, Lúcio Flávio; Vieira, Estéfano Aparecido; Tenório, Jorge Alberto Soares; Oliveira, José Roberto de

Junior, Luiz Alberto Baptista Pinto

I am this author

Grillo, Felipe Fardin

I am this author

Arrivabene, Lúcio Flávio

I am this author

Vieira, Estéfano Aparecido

39 Articles, Downloaded 14910 Times

Tenório, Jorge Alberto Soares

I am this author

Oliveira, José Roberto de

I am this author

DOI

10.5151/2594-5300-15905

Downloads

Abstract

Este estudo aborda sobre a viabilidade técnica do aproveitamento de resíduo proveniente do corte de granito para ajustar a composição química da escória de aciaria LD visando à adição no clínquer de cimento Portland. Para isso, foram realizadas a caracterização química dos resíduos e obtenção da relação CaO/SiO2 em torno de 0,9 e 1,2 para escória de aciaria LD. Foram selecionadas amostras dos resíduos, misturadas, fundidas e resfriadas em água e ao forno. Nas amostras resfriadas em água, após a análise no difratograma de raios-X, se apresentaram predominantemente amorfo. Para as amostras resfriadas ao forno, que se apresentaram cristalinas, observou-se a presença das fases mineralógicas akermanita e gehlenita, que são consideradas as fases mineralógicas ideais para a atividade hidráulica das escórias. O ajuste da composição química da escória de aciaria LD através da adição de resíduo de granito mostrou-se eficiente, indicando a sua viabilidade técnica para a fabricação de clínquer de cimento Portland.

This study focuses on the technical feasibility of utilization of waste from the cutting of granite to adjust the chemical composition of slag from steelworks LD targeting the adittion of clinker Portland cement. For that, were the chemical characterization of waste and achieve the relationship CaO/SiO2 around 0,9 to 1,2 for the steelworks slag. We selected samples of the waste, mixed, melted and cooled in water and in the oven. Samples cooled in water, after examining the diffractogram X-ray, had been predominantly amorphous. For samples cooled in the furnace, which had vitreous, there was the presence of mineralogical phases akermanita and gehlenita, which are considered as the ideal stage for the mineral water activity of the slag. The adjustment of the chemical composition of slag from steel works by the addition of waste granite was efficient, transforming the waste into a product, that's the same for blast furnace slag can be used in the manufacture of cement.

Keywords

Escória de aciaria LD; Resíduo de granito; Cimento Portland.

LD of steelworks slag; Residue of granite; Portland cement.