Title

Análise de resistência à chama de compósitos poliméricos com fibras in natura de envira cheirosa

Flame resistance analysis of polymeric composites reinforced with in natura envira cheirosa fibers

Authorship

MONTEIRO, MANOEL VINÍCIUS FRANÇA; MENDES, DAIANE DO CARMO; SILVA, NAYLANDA DAS GRAÇAS SILVA DA; SOUSA, ANA PAULA SOUZA DE; LIMA, HAYANNY BEATRIZ SARAIVA; COSTA, DEIBSON SILVA DA; CANDIDO, VERÔNICA SCARPINI

MONTEIRO, MANOEL VINÍCIUS FRANÇA

I am this author

MENDES, DAIANE DO CARMO

I am this author

SILVA, NAYLANDA DAS GRAÇAS SILVA DA

I am this author

SOUSA, ANA PAULA SOUZA DE

I am this author

LIMA, HAYANNY BEATRIZ SARAIVA

I am this author

COSTA, DEIBSON SILVA DA

I am this author

CANDIDO, VERÔNICA SCARPINI

I am this author

DOI

10.5151/2594-5327-44168

Downloads

Abstract

Este trabalho investigou a utilização de fibras naturais de envira cheirosa (Annona paludosa) como reforço em compósitos de matriz poliéster, visando avaliar seu potencial como material sustentável e resistente à chama. Os compósitos foram produzidos pelo método hand lay-up, empregando fibras curtas e longas nas frações mássicas de 1%, 3% e 5%. A caracterização morfológica das fibras foi realizada por Microscopia Eletrônica de Varredura (MEV), revelando superfície levemente rugosa e presença de deformações que favoreceram a impregnação da resina. O ensaio de flamabilidade horizontal foi conduzido conforme a norma ASTM D635. Os resultados mostraram que os compósitos apresentaram discreto aumento na taxa de propagação da chama em relação à matriz plena, porém permaneceram abaixo dos limites estabelecidos pelas normas ASTM D635 e CONTRAN. O melhor resultado foi obtido para o compósito com 5% de fibras longas, apresentando taxa de queima de 25,45 mm/min. Os resultados evidenciam o potencial das fibras de envira cheirosa para aplicação em compósitos sustentáveis com desempenho satisfatório frente à combustão.

This study investigated the use of natural envira cheirosa fibers (Annona paludosa) as reinforcement in polyester matrix composites, aiming to evaluate their potential as sustainable and flame-resistant materials. The composites were manufactured using the hand lay-up method, employing short and long fibers at mass fractions of 1%, 3%, and 5%. The morphological characterization of the fibers was performed by Scanning Electron Microscopy (SEM), revealing a slightly rough surface and the presence of deformations that favored resin impregnation. The horizontal flammability test was conducted according to the ASTM D635 standard. The results showed that the composites presented a slight increase in flame propagation rate compared to the neat matrix; however, all values remained below the limits established by ASTM D635 and CONTRAN standards. The best result was obtained for the composite containing 5% long fibers, which exhibited a burning rate of 25.45 mm/min. The findings demonstrate the potential of envira cheirosa fibers for application in sustainable composites with satisfactory combustion resistance performance.

Keywords

Envira cheirosa, Flamabilidade, Amazônia, Fibra natural

Envira cheirosa, Flammability, Amazon, Natural fiber