Title

ANÁLISE COMPARATIVA DA RESISTÊNCIA AO DESGASTE EM SUPERFÍCIES DE AÇO 1020 LUBRIFICADAS COM CONDICIONADOR DE METAIS EM RELAÇÃO À LUBRIFICAÇÃO COM GRAXA DE LÍTIO

COMPARATIVE ANALYSIS OF RESISTANCE AT WEAR IN THE SURFACE OF THE STEEL SAE 1020 LUBRICATING WITH CONDITIONER OF METAL IN RELATIONSHIP THE LUBRICATING WITH LITIO GREASE'S

Authorship

ARAUJO, MATTHEWS HENRIQUE COTA; SANTOS, ZIRLENE ALVES DA SILVA

ARAUJO, MATTHEWS HENRIQUE COTA

I am this author

SANTOS, ZIRLENE ALVES DA SILVA

I am this author

DOI

10.5151/2594-5327-40536

Downloads

Abstract

NO CENáRIO DOS SISTEMAS PRODUTIVOS INDUSTRIAIS EXISTE UM DESAFIO RELACIONADO àS PERDAS DE COMPONENTES ACOMETIDAS POR DESGASTE ABRASIVO. O DESGASTE ABRASIVO ACARRETA UM ELEVADO NúMERO DE INTERRUPçõES INESPERADAS EM MAQUINáRIOS QUE OPERAM NOS PROCESSOS E PRINCIPALMENTE QUANDO A MATéRIA PRIMA POSSUI ELEMENTOS ABRASIVOS, COMO POR EXEMPLO OS PROCESSOS DE MINERAçãO. DESTE MODO ESTA PESQUISA REALIZOU UMA ANáLISE COMPARATIVA SOBRE O DESGASTE ABRASIVO SOFRIDO PELO AçO SAE 1020 LUBRIFICADO COM CONDICIONADOR DE METAIS E POR GRAXA à BASE DE LíTIO. PARA REALIZAçãO DESTA ANáLISE COMPARATIVA FOI UTILIZADO O ABRASôMETRO QUE SEGUE OS PADRõES DA NORMA ASTM G65-16. TAL EQUIPAMENTO REALIZA TESTES COM PARâMETROS PADRONIZADOS QUE SIMULA O PROCESSO DE DESGASTE ABRASIVO. O ENSAIO REALIZADO COMPREENDE QUATRO ETAPAS DISTINTAS: A CARACTERIZAçãO DO AçO E DO ABRASIVO, A PREPARAçãO DOS CORPOS DE PROVA, A PESAGEM DO CORPO DE PROVA, A PREPARAçãO DO ABRASIVO, E A CALIBRAçãO DO EQUIPAMENTO. OS RESULTADOS DEMONSTRARAM QUE O CONDICIONADOR DE METAIS NãO TEVE UMA TAXA DE DESGASTE MENOR EM RELAçãO à GRAXA DE LíTIO. PORTANTO, PARA OS CONJUNTOS MECâNICOS QUE POSSUEM INTERAçãO E MOVIMENTO RELATIVO TANTO A GRAXA DE LíTIO QUANTO O CONDICIONADOR DE METAIS OFERECEM A MESMA RESISTêNCIA AO DESGASTE ABRASIVO

IN THE SCENARIO OF INDUSTRIAL PRODUCTION SYSTEMS, THERE IS A CHALLENGE RELATED TO THE LOSSES OF COMPONENTS CAUSED BY ABRASIVE WEAR. ABRASIVE WEAR CAUSES A HIGH NUMBER OF UNEXPECTED INTERRUPTIONS IN MACHINERY OPERATING IN PROCESSES ESPECIALLY WHEN THE RAW MATERIAL CONTAINS ABRASIVE ELEMENTS, SUCH AS MININGS PROCESSES. IN THIS WAY, THIS RESEARCH CARRIED OUT A COMPARATIVE ANALYSIS OF THE ABRASIVE WEAR SUFFERED BY SAE 1020 STEEL LUBRICATED WITH METAL CONDITIONER AND LITHIUM-BASED GREASE. TO CARRY OUT THIS COMPARATIVE ANALYSIS, AN ABRASOMETER WAS USED, WHICH FOLLOWS THE STANDARDS OF THE ASTM G65-16 STANDARD. THIS EQUIPMENT PERFORMS TESTS WITH STANDARDIZED PARAMETERS THAT SIMULATE THE ABRASIVE WEAR PROCESS. THE TEST CARRIED OUT COMPRISES FOUR DISTINCT STAGES: THE CHARACTERIZATION OF THE STEEL AND ABRASIVE, THE PREPARATION OF THE SPECIMENS, THE WEIGHING OF THE SPECIMEN, THE PREPARATION OF THE ABRASIVE, AND THE CALIBRATION OF THE EQUIPMENT. THE RESULTS DEMONSTRATED THAT THE METAL CONDITIONER DID NOT HAVE A LOWER WEAR RATE THAN LITHIUM GREASE. THUS, FOR MECHANICAL EQUIPMENT THAT HAS INTERACTION AND RELATIVE MOVEMENT, THE LITHIUM-BASE GREASE IS EQUAL TO THE PERFORMANCE OF THE METAL CONDITIONER. BOTH OFFER GOOD RESISTER ABRASIVE WEAR

Keywords

Condicionador de metais; Desgaste abrasivo; Graxa à base de lítio; ASTM G65-16

Metal conditioner; Abrasive wear; Lithium-based grease; ASTM G65-16.