ANÁLISE COMPARATIVA DA RESISTÊNCIA À CORROSÃO DE LIGAS UTILIZADAS NA INDÚSTRIA DE ÓLEO E GÁS

COMPARATIVE ANALYSIS OF CORROSION RESISTANCE OF ALLOYS USED IN THE OIL AND GAS INDUSTRY

Authorship

RIBEIRO, KÉSIA SIMÕES; SOARES, FRANCIELLY MOURA DE SOUZA; VASCONCELOS, RAFAEL DE ALMEIDA; REIS, TAMARA DA SILVA TAVARES DOS; GOMES, PATRICK DE LIMA; ELIAS, CARLOS NELSON

RIBEIRO, KÉSIA SIMÕES

I am this author

SOARES, FRANCIELLY MOURA DE SOUZA

I am this author

VASCONCELOS, RAFAEL DE ALMEIDA

I am this author

REIS, TAMARA DA SILVA TAVARES DOS

I am this author

GOMES, PATRICK DE LIMA

I am this author

ELIAS, CARLOS NELSON

I am this author

DOI

10.5151/2594-5327-40546

Downloads

Abstract

A LIGA INCONEL 625, AçO INOXIDáVEL 316L E AçO DUPLEX 2205 SãO AMPLAMENTE EMPREGADOS NA INDúSTRIA PETROQUíMICA DEVIDO à SUA ELEVADA RESISTêNCIA à CORROSãO E BOAS PROPRIEDADES MECâNICAS. A RESISTêNCIA à CORROSãO DESTAS LIGAS é ATRIBUíDA à FORMAçãO DE UM FILME DE óXIDO PASSIVO, PRINCIPALMENTE CR2O3. CONTUDO, EM AMBIENTES AGRESSIVOS CONTENDO íONS CLORETOS, COMO NO CASO DE AMBIENTES MARINHOS, ESTAS LIGAS PODEM SOFRER CORROSãO. OS íONS CLORETO COMPROMETEM A INTEGRIDADE DO FILME PASSIVO, RESULTANDO EM CORROSãO LOCALIZADA, CONHECIDA COMO CORROSãO POR PITES. ESTE TRABALHO TEVE COMO OBJETIVO AVALIAR A SUSCETIBILIDADE à CORROSãO DAS 3 CITADAS LIGAS EM UM AMBIENTE CORROSIVO SIMULANDO UM AMBIENTE MARINHO (3,5% NACL) EM TEMPERATURA AMBIENTE. FORAM CONDUZIDOS ENSAIOS ELETROQUíMICOS E ANáLISES POR MICROSCOPIA ELETRôNICA DE VARREDURA (MEV) PARA CARACTERIZAR AS MORFOLOGIAS APóS OS ENSAIOS. OS RESULTADOS INDICARAM QUE TANTO O AçO DUPLEX 2205 QUANTO A LIGA INCONEL 625 APRESENTARAM RESISTêNCIA à CORROSãO SIGNIFICATIVAMENTE MAIOR QUE O AçO INOXIDáVEL 316L. ESTE úLTIMO MOSTROU-SE SUSCETíVEL à CORROSãO POR PITES.

THE INCONEL 625 ALLOY, STAINLESS STEEL 316L, AND DUPLEX STAINLESS STEEL 2205 ARE WIDELY EMPLOYED IN THE PETROCHEMICAL INDUSTRY DUE TO THEIR HIGH CORROSION RESISTANCE AND GOOD MECHANICAL PROPERTIES. THE CORROSION RESISTANCE OF THESE ALLOYS IS ATTRIBUTED TO THE FORMATION OF A PASSIVE OXIDE FILM, MAINLY CR2O3. HOWEVER, IN AGGRESSIVE ENVIRONMENTS CONTAINING CHLORIDE IONS, SUCH AS MARINE ENVIRONMENTS, THESE ALLOYS CAN UNDERGO CORROSION. CHLORIDE IONS COMPROMISE THE INTEGRITY OF THE PASSIVE FILM, RESULTING IN LOCALIZED CORROSION, KNOWN AS PITTING CORROSION. THIS STUDY AIMED TO EVALUATE THE CORROSION SUSCEPTIBILITY OF THE MENTIONED THREE ALLOYS IN A CORROSIVE ENVIRONMENT SIMULATING A MARINE ENVIRONMENT (3.5% NACL) AT ROOM TEMPERATURE. ELECTROCHEMICAL TESTS AND SCANNING ELECTRON MICROSCOPY (SEM) ANALYSES WERE CONDUCTED TO CHARACTERIZE THE MORPHOLOGIES AFTER THE TESTS. THE RESULTS INDICATED THAT BOTH DUPLEX STAINLESS STEEL 2205 AND INCONEL 625 ALLOY EXHIBITED SIGNIFICANTLY HIGHER CORROSION RESISTANCE THAN STAINLESS STEEL 316L. THE LATTER PROVED TO BE SUSCEPTIBLE TO PITTING CORROSION..

Keywords

Corrosão; Inconel 625; Aço Duplex 2205; Aço Inoxidável 316L

Corrosion; Inconel 625; Duplex Steel 2205; 316L Stainless Steel.