Title

ANáLISE DA EFICIêNCIA DE DESSULFURAçãO NA PANELA APóS O VAZAMENTO DO AçO DO LD

ANALYSIS OF THE DESULFURIZATION EFFICIENCY IN THE LADLE AFTER STEEL TAPPING FROM LD

Authorship

Corona, Mateus Costa; Oliveira, José Roberto de; Andreatta, Vinicios; Bessa, Thiago Ribeiro; Silveira, Bruna Ramalho Ribeiro da; Dagostini, Victor Dos Santos; Miranda, Eduardo

Corona, Mateus Costa

1 Articles, Downloaded 58 Times

Oliveira, José Roberto de

I am this author

Andreatta, Vinicios

I am this author

Bessa, Thiago Ribeiro

1 Articles, Downloaded 58 Times

Silveira, Bruna Ramalho Ribeiro da

I am this author

Dagostini, Victor Dos Santos

I am this author

Miranda, Eduardo

I am this author

DOI

10.5151/2594-5300-39506

Downloads

Abstract

COM A EVOLUÇÃO DOS CLASSES DE AÇO QUE EXIGEM APLICAÇÕES ESPECÍFICAS E REQUISITOS DE ALTA QUALIDADE, CLASSES COM BAIXO TEOR DE ENXOFRE TÊM EXPRESSIVA DEMANDA CADA VEZ MAIS EXPRESSIVA. BASEADO NESTES FATOS, ESTE TRABALHO OBJETIVO AVALIAR AS PROPRIEDADES E CARACTERÍSTICAS DA ESCÓRIA FORMADA NA ETAPA DE DESSULFURIZAÇÃO DO AÇO NA PANELA, APÓS O ROSQUEAMENTO DO AÇO DO CONVERSOR PARA A PANELA, PARA UM TIPO DE AÇO COM TEOR DE ENXOFRE ALVO (S) DE 30PPM , E RELACIONÁ-LOS COM A EFICIÊNCIA DA DESULFURIZAÇÃO, QUE MEDE A CAPACIDADE DE REMOVER O ENXOFRE. A AVALIAÇÃO DAS PROPRIEDADES DA ESCÓRIA FOI REALIZADA COM O AUXÍLIO DE UM SOFTWARE DE TERMODINÂMICA COMPUTACIONAL, PARA MELHOR ENTENDIMENTO DOS FENÔMENOS QUE OCORREM NAS INTERFACES METAL-ESCÓRIA NO PROCESSO DE REFINO DO AÇO, BEM COMO NA AVALIAÇÃO DE PROPRIEDADES IMPORTANTES PARA ESTES PROCESSOS. O PARÂMETRO DO FATOR DE DESSULFURIZAÇÃO DO AÇO (SFDES) DESENVOLVIDO POR PEZZIN [1] FOI ADAPTADO PARA O CASO ONDE ALGUMAS ESCÓRIAS NÃO APRESENTAM FRAÇÃO SÓLIDA DE CAO. OS RESULTADOS CONFIRMAM QUE AS ESCÓRIAS MAIS EFICIENTES PARA A DESSULFURIZAÇÃO DO AÇO SÃO AQUELAS COM CONTEÚDO ÓTIMO DE CAO SÓLIDO E QUE O FATOR DE DESSULFURIZAÇÃO PODE SER UTILIZADO PARA AVALIAR E PREDIZER A EFICIÊNCIA DA DESSULFURIZAÇÃO DAS ESCÓRIAS ESTUDADAS.

With the evolution of the steel grades that demands specific applications and high-quality requirements, grades with low sulfur content have had an expressive increasingly demand. Based on these facts, this work aims to evaluate the properties and characteristics of the slag formed in the steel desulfurization step in the ladle, after the steel tapping from converter to ladle, for a steel grade with a target sulfur content (S) of 30ppm, and relate them to the efficiency of desulfurization, which measures the ability to remove sulfur. The evaluation of the slag properties was performed with the aid of a computational thermodynamics’ software, for a better understanding of the phenomena that occur at the metal-slag interfaces in the steel refining process, as well as in the evaluation of important properties for these processes. The Steel Desulfurization Factor (SFDeS) parameter developed by Pezzin [1] was adapted for the case where some slags do not have a solid CaO fraction. The results confirmed that the most efficient slags for steel desulfurization are those with an optimal solid CaO content and that the Desulfurization Factor can be used to evaluate and predict the desulfurization efficiency for the studied slags.

Keywords

Eficiência de dessulfuração; Metalurgia secundária; escória de topo

Steel desulfurization efficiency; Secondary metallurgy; Top slag.