Title

ANÁLISE DA INFLUÊNCIA DOS CICLOS TÉRMICOS DE DIFERENTES PROJETOS DE FORNOS DE RECOZIMENTO CONTÍNUO NA MICROESTRUTURA E PROPRIEDADES MECÂNICAS DE AÇOS DUAL PHASE GALVANIZADOS – ARCELORMITTAL VEJA

ANALYSYS OF THE TERMAL CICLES INFLUENCE OF DIFFERENT CONTINUOS ANNEALING FURNACES PROJECTS IN MICROESTRUCTURE AND MECHANICAL PROPERTIES OF DUAL PHASE STEELS – ARCELORMITTAL VEJA

Authorship

Oliveira, Fernando Coelho de; Miranda, Fabiano Jose Fabri; Souza, Fabrício Brandão Pereira de; Drumond, Julliovany; Santos., Dagoberto Brandão

Oliveira, Fernando Coelho de

I am this author

Miranda, Fabiano Jose Fabri

I am this author

Souza, Fabrício Brandão Pereira de

I am this author

Drumond, Julliovany

I am this author

Santos., Dagoberto Brandão

I am this author

DOI

10.5151/2594-5297-22557

Downloads

Abstract

A indústria automobilística está cada vez mais competitiva e com isso as empresas siderúrgicas estão investindo no desenvolvimento de aços de alta resistência, como os aços Dual Phase, que apresentam uma boa combinação de resistência, conformabilidade e soldabilidade. Este trabalho tem por objetivo apresentar os resultados de um plano de experiência industrial realizado em linhas de galvanização por imersão à quente, onde foi verificada a influência do perfil térmico de diferentes projetos de fornos de recozimento contínuo na microestrutura e propriedades mecânicas de aços Dual Phase galvanizados. Foram realizados ensaios mecânicos e caracterização da microestrutura. Os resultados mostram que altas taxas de aquecimento, durante o recozimento em temperaturas intercríticas, altas taxas de resfriamento e baixo tempo de equalização propiciam uma microestrutura com maior volume de martensita e, como consequência, valores maiores de limite de resistência .

The automotive industry has increasing their competitive and the steel companies are investing the development of high strength steels such as dual phase steels, which have a good combination of strength, formability and weldability. This work has for objective to present the results of an experience in an industrial plant carried out in lines of the hot dip galvanizing; where it was verified the influence of the thermal profile of different designs of continuous annealing furnaces on the microstructure and mechanical properties of dual phase steels galvanized. Mechanical tests and microstructure characterization were performed. The results show that high heating rates during the annealing at intercritical temperatures, low equalization time and high cooling rates provide a microstructure with a greater volume fraction of martensite and, consequently, higher values of tensile strength.

Keywords

Aços dual phase; Recozimento contínuo; Microestrutura; Propriedades mecânicas.

Dual phase steel; Continuous annealing; Microstructure; Mechanical properties.