Title

ANÁLISE DA RESISTÊNCIA A COMPRESSÃO DE COMPÓSITO DE MATRIZ DE POLIURETANO REFORÇADO LONGITUDINALMENTE COM COLMOS DE SORGO VASSOURA

ANALYSIS OF THE COMPRESSIVE STRENGTH OF POLYURETHANE MATRIX COMPOSITES LONGITUDINALLY REINFORCED WITH BROOMCORN STALKS

Authorship

SATIRO, ANTONIO RICARDO GRIPPA; CARVALHO, EDUARDO ATEM DE; LOPES, FELIPE PERISSÉ DUARTE; SIMONASSI, NOAN TONINI; MONTEIRO, SERGIO NEVES

SATIRO, ANTONIO RICARDO GRIPPA

I am this author

CARVALHO, EDUARDO ATEM DE

I am this author

LOPES, FELIPE PERISSÉ DUARTE

I am this author

SIMONASSI, NOAN TONINI

I am this author

MONTEIRO, SERGIO NEVES

I am this author

DOI

10.5151/2594-5327-41020

Downloads

Abstract

A CRESCENTE DEMANDA POR MATERIAIS SUSTENTáVEIS TEM IMPULSIONADO PESQUISAS EM COMPóSITOS POLIMéRICOS REFORçADOS COM FIBRAS NATURAIS. ESTE TRABALHO INVESTIGA O COMPORTAMENTO DE COMPóSITOS DE MATRIZ POLIURETANO REFORçADOS COM COLMOS DE SORGO VASSOURA (SORGHUM BICOLOR) EM DIFERENTES FRAçõES VOLUMéTRICAS SOB FORçAS COMPRESSIVAS. UTILIZOU-SE UMA RESINA DE POLIURETANO à BASE DE óLEO DE MAMONA E COLMOS DOADOS POR PRODUTORES INDEPENDENTES. OS COMPóSITOS FORAM MOLDADOS, CURADOS E CORTADOS CONFORME A NORMA ASTM D695, E SUBMETIDOS A ENSAIOS DE COMPRESSãO. OS RESULTADOS MOSTRARAM QUE A RESISTêNCIA à COMPRESSãO AUMENTOU COM A FRAçãO VOLUMéTRICA DE COLMOS, COM VALORES VARIANDO DE 3,97 MPA A 6,01 MPA. A ANáLISE DE ANOVA CONFIRMOU DIFERENçAS ESTATISTICAMENTE SIGNIFICATIVAS ENTRE OS NíVEIS DE REFORçO. A RESISTêNCIA à COMPRESSãO ESPECíFICA TAMBéM SEGUIU A MESMA TENDêNCIA, VALIDANDO A EFICáCIA DO SORGO VASSOURA COMO MATERIAL DE REFORçO. FOI CONCLUíDO QUE A INCORPORAçãO DE COLMOS DE SORGO VASSOURA NãO Só MELHOROU AS PROPRIEDADES MECâNICAS DOS COMPóSITOS, MAS TAMBéM CONTRIBUIU PARA A SUSTENTABILIDADE AMBIENTAL, OFERECENDO UMA SOLUçãO VIáVEL PARA USO DO COLMO.

THE GROWING DEMAND FOR SUSTAINABLE MATERIALS HAS DRIVEN RESEARCH INTO POLYMER COMPOSITES REINFORCED WITH NATURAL FIBERS. THIS WORK INVESTIGATES THE BEHAVIOR OF POLYURETHANE MATRIX COMPOSITES REINFORCED WITH BROOMCORN (SORGHUM BICOLOR) STALKS IN DIFFERENT VOLUME FRACTIONS UNDER COMPRESSIVE FORCES. A POLYURETHANE RESIN BASED ON CASTOR OIL AND STALKS DONATED BY INDEPENDENT PRODUCERS WERE USED. THE COMPOSITES WERE MOLDED, CURED, AND CUT ACCORDING TO ASTM D695 STANDARDS, AND SUBJECTED TO COMPRESSION TESTS. THE RESULTS SHOWED THAT THE COMPRESSIVE STRENGTH INCREASED WITH THE VOLUMETRIC FRACTION OF STALKS, WITH VALUES RANGING FROM 3.97 MPA TO 6.01 MPA. ANOVA ANALYSIS CONFIRMED STATISTICALLY SIGNIFICANT DIFFERENCES BETWEEN REINFORCEMENT LEVELS. THE SPECIFIC COMPRESSIVE STRENGTH ALSO FOLLOWED THE SAME TREND, VALIDATING THE EFFECTIVENESS OF BROOMCORN AS A REINFORCING MATERIAL. IT WAS CONCLUDED THAT THE INCORPORATION OF BROOMCORN STALKS NOT ONLY IMPROVED THE MECHANICAL PROPERTIES OF THE COMPOSITES BUT ALSO CONTRIBUTED TO ENVIRONMENTAL SUSTAINABILITY, OFFERING A VIABLE SOLUTION FOR THE USE OF STALKS.

Keywords

Compósito polimérico; Sorgo vassoura; Resistência a compressão.

Polymeric composite; Broomcorn sorghum; compressive strength.