ANÁLISE DA TRANSFERÊNCIA DE Si DA INJEÇÃO DE CARVÃO PULVERIZADO PARA O GUSA CONSIDERANDO O SISTEMA CaO-SiO2-Al2O3

EVALUATION ON Si TRANSFER FROM INJECTED PULVERIZED COAL TO IRON INCORPORATING THE THERMODYNAMIC SYSTEM CaO-SiO2-Al2O3

Authorship

Heck, Nestor Cezar; Perli, Gabriel Silva

Heck, Nestor Cezar

I am this author

Perli, Gabriel Silva

I am this author

DOI

10.5151/2594-5327-17986

Downloads

Abstract

Outro estudo da redução carbotérmica no alto-forno, que pode resultar na transferência de Si, da matéria mineral do carvão pulverizado (da injeção de carvão pulverizado) ao ferro gusa, foi feito por meio da termodinâmica computacional, levando em conta o sistema SiO2-CaO-Al2O3. A técnica de injeção de carvão pulverizado, ICP, reduz os custos com o coque e diminui a emissão de CO2 da coqueria. O conteúdo de Si no metal fundido, por outro lado, tende a aumentar com a injeção intensiva de carvão e deteriora a boa prática na aciaria porque aumenta a quantidade de escória na ala de refino. O sistema estendido Fe-CO-Si-Al-Ca foi utilizado nesta análise termodinâmica que usou frações mássicas escolhidas de carbono e de SiO2 (e mais tarde Al2O3 e CaO), balanço FeO, como dados de entrada para as simulações. Os resultados preliminares mostram que, tendo a porcentagem de SiO2 como variável, para as composições selecionadas, sob condições fortemente redutoras e na presença de carbono livre, minerais do carvão injetado no forno podem ter um papel importante na transferência de Si, das cinzas para o ferro gusa.

Another study was made by means of the computational thermodynamic, incorporating the SiO2-CaO-Al2O3 system, of the carbothermic reduction in the blast furnace which could lead to the Si transfer from the mineral matter of the pulverized coal (from the coal injection) into the hot metal. Pulverized coal injection technique, PCI, lowers the coke derived costs and decreases the emission of CO2 from coke ovens. Si content in molten metal, on the other hand, tends to increase with intensive coal injection and deteriorates the good steelmaking practice because it raises the slag amount in the refining shop. The extended Fe-C-O-Si-Al-Ca system has been used in this thermodynamic analysis which used selected carbon mass fractions and some amounts of SiO2 (later Al2O3 and CaO), balance FeO, as input for simulations. Preliminary results show, using the percentage of SiO2 as variable, that, for the selected compositions, under strongly reducing conditions and in the presence of free carbon, minerals from the coal injected into blast furnace may have an important role in Si transfer from ash into the hot metal.