ANÁLISE DA VARIAÇÃO DE TEMPERATURA DE QUEIMA NAS PROPRIEDADES DA CERÂMICA VERMELHA

ANALYSIS OF BURNING TEMPERATURE VARIATION IN THE PROPERTIES OF RED CERAMIC CERAMIC

Authorship

RISCADO, ANA LAURA LOPES DE MATOS; AMARAL, IULLY DA SILVA; PEREIRA, MARIA MARIANA DIAS; VIEIRA, CARLOS MAURÍCIO FONTES; MARVILA, MARKSSUEL TEIXEIRA

RISCADO, ANA LAURA LOPES DE MATOS

I am this author

AMARAL, IULLY DA SILVA

I am this author

PEREIRA, MARIA MARIANA DIAS

I am this author

VIEIRA, CARLOS MAURÍCIO FONTES

I am this author

MARVILA, MARKSSUEL TEIXEIRA

I am this author

DOI

10.5151/2594-5327-40609

Downloads

Abstract

A INDúSTRIA DA CERâMICA VERMELHA é MUITO DIVERSA EM TERMOS DE SETORES, MATéRIAS-PRIMAS E PRODUTOS FINAIS. O MUNICíPIO DE CAMPOS DOS GOYTACAZES é UM IMPORTANTE CENTRO DESSA INDúSTRIA, DEVIDO à ABUNDâNCIA DE ARGILA NA REGIãO. UM ASPECTO IMPORTANTE DA FABRICAçãO DE PEçAS CERâMICAS é O CONTROLE DAS TEMPERATURAS DURANTE O PROCESSO DE QUEIMA, PARA EVITAR DEFEITOS NOS PRODUTOS FINAIS DEVIDO A TENSõES RESULTANTES DA EXPANSãO TéRMICA. O SEGUINTE ESTUDO FOI REALIZADO PARA ANALISAR O DESENVOLVIMENTO E CARACTERIZAçãO DE CERâMICA VERMELHA QUEIMADA EM DIFERENTES TEMPERATURAS, BUSCANDO GARANTIR BOAS PROPRIEDADES DENTRO DAS DENSIDADES REQUERIDAS. OS CORPOS CERâMICOS FORAM FABRICADOS ATRAVéS DE PRENSAGEM VIA SECA E FORAM AVALIADOS ATRAVéS DAS SEGUINTES PROPRIEDADES: RETRAçãO LINEAR, ABSORçãO DE áGUA, POROSIDADE APARENTE E RESISTêNCIA à TRAçãO POR COMPRESSãO DIAMETRAL COM ANáLISE DO MóDULO DE WEIBULL. A RETRAçãO LINEAR AUMENTOU COM O AUMENTO DA TEMPERATURA DE QUEIMA. A ABSORçãO DE áGUA E A POROSIDADE FORAM MAIORES PARA AS PEçAS QUEIMADAS EM 900ºC. EM SE TRATANDO DA RESISTêNCIA à TRAçãO POR COMPRESSãO DIAMETRAL, HOUVE AUMENTO DA RESISTêNCIA CONFORME O AUMENTO DA TEMPERATURA DE QUEIMA, E TODAS AS TEMPERATURAS GERARAM RESISTêNCIA SUFICIENTE PARA PRODUçãO DE TIJOLOS DE ALVENARIA.

THE RED CERAMICS INDUSTRY IS VERY DIVERSE IN TERMS OF SECTORS, RAW MATERIALS AND FINAL PRODUCTS. THE MUNICIPALITY OF CAMPOS DOS GOYTACAZES IS AN IMPORTANT CENTER FOR THIS INDUSTRY, DUE TO THE ABUNDANCE OF CLAY IN THE REGION. AN IMPORTANT ASPECT OF MANUFACTURING CERAMIC PARTS IS CONTROLLING TEMPERATURES DURING THE FIRING PROCESS, TO AVOID DEFECTS IN THE FINAL PRODUCTS DUE TO STRESSES RESULTING FROM THERMAL EXPANSION. THE FOLLOWING STUDY WAS CARRIED OUT TO ANALYZE THE DEVELOPMENT AND CHARACTERIZATION OF RED CERAMIC FIRED AT DIFFERENT TEMPERATURES, SEEKING TO GUARANTEE GOOD PROPERTIES WITHIN THE REQUIRED DENSITIES. THE CERAMIC BODIES WERE MANUFACTURED USING DRY PRESSING AND WERE EVALUATED BASED ON THE FOLLOWING PROPERTIES: LINEAR SHRINKAGE, WATER ABSORPTION, APPARENT POROSITY AND TENSILE STRENGTH BY DIAMETRICAL COMPRESSION. LINEAR SHRINKAGE INCREASED WITH INCREASING FIRING TEMPERATURE. WATER ABSORPTION AND POROSITY WERE GREATER FOR PIECES FIRED AT 900ºC. WHEN IT COMES TO TENSILE STRENGTH DUE TO DIAMETRICAL COMPRESSION, THERE WAS AN INCREASE IN RESISTANCE AS THE FIRING TEMPERATURE INCREASED, AND ALL TEMPERATURES GENERATED SUFFICIENT RESISTANCE FOR THE PRODUCTION OF MASONRY BRICKS.

Keywords

Cerâmica vermelha; Processo de queima; Argila.

Red ceramic; Burning process; Clay.