ANÁLISE DA VELOCIDADE E DA CONSTANTE DE VELOCIDADE DA REAÇÃO DE REVERSÃO DE ENXOFRE PARA MISTURA A BASE DE CAO E MGO

ANALYSIS OF THE SPEED AND SPEED CONSTANT OF THE REVERSAL REACTION OF SULFUR FOR MIXTURES BASED CAO AND MGO

Authorship

Klippel, Cynara Christ

Klippel, Cynara Christ

I am this author

DOI

10.5151/2594-5300-34857

Downloads

Abstract

O TRABALHO TEM COMO OBJETIVO ANALISAR A VELOCIDADE DA REAçãO DE REVERSãO DE ENXOFRE PARA MISTURAS A BASE DE CAO E MGO. FORAM REALIZADOS TESTES COM DIFERENTES MISTURAS, VARIANDO A QUANTIDADE DE CADA MATERIAL A SER ADICIONADO, CONFORME ELE é ADICIONADO INDUSTRIALMENTE. AMOSTRAS DE METAL FORAM COLETADAS PARA VERIFICAR A VARIAçãO DO TEOR DE ENXOFRE NO AçO AO LONGO DO TEMPO DO EXPERIMENTO. OBSERVOU-SE QUE AS MATéRIAS-PRIMAS QUE TIVERAM MAIOR REVERSãO FORAM AS QUE TIVERAM AS MAIORES VELOCIDADES. PARA TODAS AS MISTURAS, A MAIOR REVERSãO OCORREU NOS PRIMEIROS 5 MINUTOS. NO CASO DESTAS MATéRIAS-PRIMAS ESTUDADAS, AS MISTURAS COM BASICIDADE 3,2 APRESENTARAM MENOR REVERSãO DE ENXOFRE, POIS FORAM AS QUE OBTIVERAM: MAIOR PORCENTAGEM DE FASE SóLIDA E VISCOSIDADE, O QUE DIMINUI O VALOR DA CONSTANTE DE VELOCIDADE K.

THE WORK AIMS TO ANALYZE THE SPEED OF THE SULFUR REVERSION REACTION FOR MIXTURES BASED ON CAO AND MGO. TESTS WERE CARRIED OUT WITH DIFFERENT MIXTURES, VARYING THE AMOUNT OF EACH MATERIAL TO BE ADDED, AS IT IS INDUSTRIALLY ADDED. METAL SAMPLES WERE COLLECTED TO VERIFY THE VARIATION IN THE SULFUR CONTENT OF THE STEEL OVER THE TIME OF THE EXPERIMENT. IT WAS OBSERVED THAT THE RAW MATERIALS THAT HAD THE GREATEST REVERSAL WERE THE ONES THAT HAD THE GREATEST SPEEDS. FOR ALL MIXTURES, REVERSAL OCCURRED WITHIN THE FIRST 5 MINUTES. IN THE CASE OF THESE RAW MATERIALS STUDIED, THE MIXTURES WITH BASICITY 3.2 PRESENTED LESS SULFUR REVERSION, AS THEY WERE THE ONES THAT OBTAINED: HIGHER PERCENTAGE OF SOLID PHASE AND VISCOSITY, WHICH DECREASES THE VALUE OF THE VELOCITY CONSTANT K.

Keywords

Reversão do enxofre; Dessulfuração; Termodinâmica Computacional; Constante de Velocidade

Sulfur reversion; Desulfurization; Computational Thermodynamics; Constant of Speed