ANÁLISE DAS PROPRIEDADES MECÂNICAS DE SCAFFOLDS ESTRUTURADOS POR GEOMETRIAS TPMS

ANALYSIS OF MECHANICAL PROPERTIES OF SCAFFOLDS STRUCTURED BY TPMS GEOMETRIES

Authorship

SOARES, EDSON MIRANDA; CONCEIÇÃO, ANA BEATRIZ DAS NEVES; PINHEIRO, MIRIANE ALEXANDRINO; SILVA, ALISSON CLAY RIOS DA; CANDIDO, VERÔNICA SCARPINI

SOARES, EDSON MIRANDA

I am this author

CONCEIÇÃO, ANA BEATRIZ DAS NEVES

I am this author

PINHEIRO, MIRIANE ALEXANDRINO

I am this author

SILVA, ALISSON CLAY RIOS DA

I am this author

CANDIDO, VERÔNICA SCARPINI

I am this author

DOI

10.5151/2594-5327-41534

Downloads

Abstract

O PRESENTE ARTIGO BUSCA AVALIAR SCAFFOLDS ESTRUTURADOS COM GEOMETRIAS TPMS SOBRE A INFLUêNCIA DE CARGA UNIAXIAL COMPRESSIVA. PARA ISSO, FORAM PROJETADOS TRêS MODELOS DISTINTOS DE SCAFFOLDS ESTRUTURADOS COM OS FORMATOS GIRóIDE, SCHWARZ PRIMITIVO E IWP PARA A REALIZAçãO DE TESTES MECâNICOS, SEGUINDO A NORMA ASTM D695-15. OS RESULTADOS REVELARAM QUE AS AMOSTRAS COMPOSTAS PELA ESTRUTURA SCHWARZ PRIMITIVO APRESENTOU OS MELHORES ATRIBUTOS PARA O EMPREGO COMO SCAFFOLD, POSSUINDO MóDULO DE COMPRESSãO DE 0,349 GPA , RESISTêNCIA A COMPRESSãO DE 11,937 MPA E DEFORMAçãO UNIFORME DE 0,07276. AS DEMAIS AMOSTRAS TAMBéM APRESENTARAM RESULTADOS SATISFATóRIOS, PORéM, OS SCAFFOLDS ESTRUTURADOS COM A GEOMETRIA IWP APRESENTARAM CARACTERíSTICA PARTICULAR DE DEFORMAçãO UNIFORME, EM RELAçãO AS DEMAIS AMOSTRAS, OBTENDO DEFORMAçãO DE 0,11025.

THIS ARTICLE AIMS TO EVALUATE SCAFFOLDS STRUCTURED WITH TPMS GEOMETRIES UNDER THE INFLUENCE OF UNIAXIAL COMPRESSIVE LOAD. FOR THIS PURPOSE, THREE DIFFERENT MODELS OF SCAFFOLDS STRUCTURED WITH GYROID, PRIMITIVE SCHWARZ AND IWP FORMATS WERE DESIGNED FOR MECHANICAL TESTS, FOLLOWING THE ASTM D695-15 STANDARD. THE RESULTS REVEALED THAT THE SAMPLES COMPOSED OF THE PRIMITIVE SCHWARZ STRUCTURE PRESENTED THE BEST ATTRIBUTES FOR USE AS SCAFFOLD, HAVING A COMPRESSION MODULUS OF 0.349 GPA, COMPRESSIVE STRENGTH OF 11.937 MPA AND UNIFORM DEFORMATION OF 0.07276. THE OTHER SAMPLES ALSO PRESENTED SATISFACTORY RESULTS, HOWEVER, THE SCAFFOLDS STRUCTURED WITH THE IWP GEOMETRY PRESENTED A PARTICULAR CHARACTERISTIC OF UNIFORM DEFORMATION, IN RELATION TO THE OTHER SAMPLES, OBTAINING A DEFORMATION OF 0.11025.

Keywords

Scaffold; TPMS; Impressão 3D; ASTM D695.

Scaffold; TPMS; 3D Printing; ASTM D695.