ANÁLISE DE FALHA DE ROLOS CLASSIFICADORES DE PELOTAS DE MINÉRIO DE FERRO

FAILURE ANALYSIS OF CLASSIFYING ROLLERS OF IRON ORE PELLETS

Authorship

Milan, Marcelo Tadeu; Maluf, Omar; Tarpani, José Ricardo; Valfre, Jair; Cesário, Cláudio

Milan, Marcelo Tadeu

I am this author

Maluf, Omar

I am this author

Tarpani, José Ricardo

I am this author

Valfre, Jair

I am this author

Cesário, Cláudio

I am this author

DOI

10.5151/2594-5327-0476

Downloads

Abstract

Rolos classificadores de pelotas de minério de ferro apresentaram intenso desgaste superficial, associado à intensa agregação de partículas de minério. Determinou-se que a presença de ferrita e de vazios de fundição no aço, alem da excessiva rugosidade superficial podem ter contribuído para o efeito de ancoramento de partículas. O mecanismo básico de dano dos rolos foi o de desgaste abrasivo livre a dois corpos, com perda de massa via sulcamento e riscamento da matriz por partículas de minério. Concluiu-se que o espaçamento entre os precipitados de carbonetos no aço e grande o suficiente para permitir tais fenômenos. Foi recomendado o uso de um aço mais duro, com uma distribuição mais refinada de carbonetos fortalecedores, e sugerida a aplicação de um revestimento de alta dureza, com os devidos cuidados quanto às propriedades magnéticas e acabamento superficial finais.

Classifying rollers of iron ore pellets presented surface wear, alongside iron ore particle agglomeration. It was determined that the presence of ferrite and casting defects in the microstructure, besides excessive surface roughness, may have contributed to the anchorage effect of the particles. The basic wear mechanism on the rollers was two body abrasion, where weight loss was mainly caused by scratching and plowing of the austenite matrix by the iron ore particles. It was conclude that the carbide interparticle spacing within the matrix was large enough to allow such phenomena to take place. Harder steel was recommended, with a finer carbide distribution, and a hard coating was also suggested, taking the necessary precautions regarding final magnetic and surface finishing properties.

Keywords

Aço inoxidável; Análise de falha; Componente rotativo; Desgaste; Revestimento.

Coating; Failure analysis; Rotating component; Stainless steel; Wear.