Title

ANÁLISE DE FALHA METALÚRGICA EM PARAFUSOS DE CASCA ACETABULAR METÁLICA

FAILURE ANALYSIS OF METALLURGICAL IN BOLTS SHELL ACETABULAR METALLIC

Authorship

Azevedo, Thiago Figueiredo; Santos, Silvando Vieira dos; Andrade, Carlos Eduardo Celestino de; Strohaecker, Telmo Roberto; Griza, Sandro; Ueki, Marcelo Massayoshi

Azevedo, Thiago Figueiredo

I am this author

Santos, Silvando Vieira dos

I am this author

Andrade, Carlos Eduardo Celestino de

I am this author

Strohaecker, Telmo Roberto

I am this author

Griza, Sandro

I am this author

Ueki, Marcelo Massayoshi

I am this author

DOI

10.5151/2594-5327-23234

Downloads

Abstract

Parafusos são, muitas vezes, usados para aumentar a estabilidade da fixação da casca acetabular metálica em artroplastia total do quadril não cimentada. Este estudo teve como objetivo identificar os fatores metalúrgicos associados a dois casos de fraturas de parafusos de casca acetabularde artroplastia total do quadril revisadas prematuramente. Foram realizadas análises preliminares das radiografias e das peças revisadas. Os parafusos fraturados foram submetidos à análise de fratura, microssonda EDS e metalografias. Dois fatores foram identificados: microestrutura de liga de titânio consistindo em placas da fase alfa com camada rica em oxigênio e liga de Cr-Co com microestrutura dendrítica e formação de microrechupes desfavoravelmente alinhados.

Screws are often used in total hip arthroplasty to increase the cementlessacetabularmetal backed fixation stability. This study aimed at identifying metallurgical factors related to metal backed screw fractures in two cases of premature total hip arthroplastyrevision. It was performed a preliminary analysis of radiographs and retrieved parts.Fractured screws were subjected to fracture analysis, EDS microprobe andmetallographic. A finite element analysis was performed to predict the stresses experienced by the screws. Two factors were identified: titanium alloy microstructure consisting of alpha phase plates with oxygen-rich alpha case and as cast Cr-Co alloy with dendritic microstructure and unfavorably aligned shrinkage formation.

Keywords

Parafusos;Acetabulo;Fadiga.

THA; Metal backed screws; Fatigue; Ti6Al4V; Cr-Co.