ANÁLISE DE FILME CONTÍNUO ATRAVÉS DA PERFILOMETRIA E DE MEV/EDS EM CONCRETO C30 SUBMETIDO À AGRESSIVIDADE CLASSE III

ANALYSIS OF CONTINUOUS FILM THROUGH THE PROFILEMETRY AND MEV/EDS IN C30 CONCRETE SUBMITTED TO CLASS III AGGRESSIVENESS

Authorship

Couto, Carmen; Silva, Joana Darc; Godoy, G. Cristina; Fontes, Roberto; Flor, Jacqueline

Couto, Carmen

I am this author

Silva, Joana Darc

I am this author

Godoy, G. Cristina

I am this author

Fontes, Roberto

I am this author

Flor, Jacqueline

I am this author

DOI

10.5151/2594-5327-14683

Downloads

Abstract

Este trabalho tem como objetivo avaliar um concreto C30, NBR-8953 "Concreto para Fins Estruturais", o qual foi produzido com um fator água-cimento de 0,50. A avaliação da degradação do concreto foi feita em corpos de prova protegidos por filme contínuo, através da perfilometria e de MEV/EDS. A resistência à compressão de 30MPa foi obtida em função da dosagem proposta e de cuidados referentes à produção propriamente dita. Os corpos de prova foram submetidos a meio agressivo ácido (H SO -2,5%) por imersão, com e sem (hidrofugante silano-siloxano), associado à tinta acrílica (resina acrílica em solvente), foi avaliado através de imagens em 3D, parâmetros de amplitude topográficos e de MEV/EDS.As imagens e os parâmetros de amplitude gerados pelo perfilômetro permitiram ter uma clara visão do processo de degradação do concreto atacado por ácido, e a minimização deste efeito, comprovada por uma menor variação dos parâmetros de amplitude e pela manutenção da integridade da camada protetora visualizada e analisada pelo MEV/EDS. A metodologia proposta neste trabalho demonstra que a associação de métodos já consagrados na metalurgia, perfilometria e MEV/EDS, podem contribuir significativamente em pesquisas sobre a durabilidade do concreto.

The present work aims to evaluate the C30 concrete, NBR-8953 "Concrete for Structural Purposes", which was produced with a water-cement factor of 0.50. The concrete degradation assessment was made in tests specimens protected by continuous film, through profilemetry and MEV/EDS. The resistance to compression of 30MPa was obtained according to the proposal dosage and the care for the production itself. The tests specimens were submitted to aggressive acid environment (H SO - 24 2,5%) by immersion, with and without protective layer. The continuous film formed by a composition- based sealer (silane-siloxane), associated with the acrylic paint (acrylic resin in solvent), was evaluated by means of 3D images, topographical amplitude parameters and MEV/EDS. The images and the amplitude parameters generated by profilometer allowed to have a clear vision of the process of the concrete degradation attacked by acid, and the minimization of this effect, proven by a lesser variation of the amplitude parameters and by the maintenance of the integrity of the protective layer visualized and analyzed by the MEV/EDS. The methodology proposed in this work demonstrates that the association of methods already renowned in metallurgy, profilemetry and MEV/ EDS, can contribute significantly in research on the concrete durability.

Keywords

Durabilidade do concreto; Perfilometria; Microscopia eletrônica; Superfície protetora.

Concrete Durability, Profilemetry, Electronic Microscopy, Protective Surface Layer.