Title

ANÁLISE DO EFEITO DA VARIAÇÃO DO TEOR DE Cu NA TRABALHABILIDADE DA LIGA Al-Mg-Cu

ANALYSIS OF THE EFFECT OF THE VARIATION IN CONTENT OF Cu ON WORKABILITY OF THE Al-Mg-Cu ALLOY

DOI

10.5151/2594-5297-15690

Downloads

Abstract

A presente pesquisa tem como objetivo analisar o efeito de diferentes teores de Cobre na trabalhabilidade da liga Al-Mg-Cu submetida a um processo de laminação a frio, bem como, fazer uma comparação com a liga Al-Mg-Si (6101), comumente utilizada na indústria para a fabricação de cabos condutores de energia elétrica. Foram feitas ligas bases de alumínio com 0,6% Mg e posteriormente modificou-se com Cu nos teores de 2,2; 1,8; 1,0; 0,6 e 0,3%, em um molde com formato de “U”. Após a usinagem os corpos de prova foram laminados a frio, em um laminador com canal circular, sendo feitos sucessivos passes até chegarem a fios de aproximadamente 3,90 mm de diâmetro. Os fios passaram por um rápido tratamento térmico a 230oC por 1h. As amostras foram submetidas a um ensaio de tração, antes e após o tratamento, a fim de se avaliar as respostas das propriedades mecânicas do material perante o tratamento térmico. Também foram feitos testes de condutividade elétrica nos fios da liga. A partir dos resultados obtidos foi possível observar que a liga Al-Mg-Cu possui boa trabalhabilidade, em todos os percentuais de Cobre, a liga com 0,3% de Cu apresentou condutividade elétrica que atende à norma para fios de liga 6101, porém o seu Limite de Resistência à Tração (LRT) ficou abaixo do esperado para fios de liga 6101, com diâmetros acima de 3,50 mm.

 

This research aims to analyze the effect of different levels of copper in the workability of the alloy Al-Mg-Cu subjected to a process of cold rolling, and make a comparison with the Al-Mg-Si (6101) alloy, commonly used in industry for the manufacture of cable conductors of electricity. Bases were made of aluminum alloy with 0.6% Mg and was later modified with the Cu content of 2.2, 1.8, 1.0, 0.6 and 0.3%, in a mold with format " U ". After the machinability, the specimens were cold rolled until arrive in wires with 3.90mm of diameter. The wires passed for a heat treatment at 230°C for 1 h. Traction tests were made, before and after treatment in order to evaluate the responses of the mechanical properties of the material before the heat treatment. Tests were also made in the electrical conductivity of the alloy wire. From the results it was possible to observe that the Al-Mg-Cu alloy has good workability, in all of Cu contents. The 0.3%Cu alloy presented good electrical conductibility that answers to 6101 alloy wire standards, but the tensile strength was below of the waited for 6101 alloy wires, with diameters greater than 3.90 mm.

Keywords

Trabalhabilidade; Laminação a frio; Tratamento térmico.

Workability; Cold rolled; Heat treatment.

How to refer

Santos, Washington Luis Reis; Feitosa, Johnyson Pereira; Santos, Emerson David Cavalcante; Freitas, Emmanuelle Sá; Quaresma, José Maria do Vale. ANÁLISE DO EFEITO DA VARIAÇÃO DO TEOR DE Cu NA TRABALHABILIDADE DA LIGA Al-Mg-Cu , p. 544-550. In: 46º Seminário de Laminação, Processos e Produtos Laminados e Reviestidos, Santos, 2009.
ISSN: 2594-5297 , DOI 10.5151/2594-5297-15690