Title

ANÁLISE METALÚRGICA DE SEGREGAÇÃO CENTRAL EM PLACAS

METALLURGICAL ANALYSIS OF SLAB CENTERLINE SEGREGATION

Authorship

Martins, Ricardo Vieira Regis de Almeida

Martins, Ricardo Vieira Regis de Almeida

I am this author

DOI

10.5151/2594-5300-40353

Downloads

Abstract

ENQUANTO O AÇO LÍQUIDO PRODUZIDO NOS PADRÕES DO ESTADO DA ARTE É ESSENCIALMENTE HOMOGÊNEO, A SOLIDIFICAÇÃO RESULTA NA PARTIÇÃO DE ELEMENTOS QUÍMICOS. UM EFEITO DESSA SOLIDIFICAÇÃO HETEROGÊNEA É A FORMAÇÃO DE SEGREGAÇÃO NA LINHA CENTRAL DA PLACA. A SEGREGAÇÃO CENTRAL É PROBLEMÁTICA, PODENDO RESULTAR EM MICROESTRUTURAS FRÁGEIS QUE SÃO HERDADAS PELOS PRODUTOS FINAIS E ATÉ MESMO NA GERAÇÃO DE TRINCAS. EM BUSCA DA MELHORIA CONTÍNUA NA QUALIDADE DO AÇO, É NECESSÁRIO COMPREENDER ESSE FENÔMENO EM SUA DIMENSÃO METALÚRGICA. ESTE ARTIGO TEM COMO OBJETIVO CARACTERIZAR ESSE FENÔMENO UTILIZANDO TÉCNICAS DE MICROSCOPIA, TANTO ÓPTICA QUANTO ELETRÔNICA DE VARREDURA (SEM), AVALIANDO A MICROESTRUTURA DO MATERIAL BASE E DAS ZONAS DE SEGREGAÇÃO NA LINHA CENTRAL, BEM COMO SUA CORRELAÇÃO COM A COMPOSIÇÃO QUÍMICA E MICRODUREZA.

While liquid steel at the state-of-the-art is essentially homogeneous, solidification results in partitioning of chemical elements. One effect of this heterogeneous solidification is the formation of Slab Centerline Segregation. Centerline segregation is a serious issue, as it can lead to brittle microstructures that are inherited by the final steel products and even to the appearance of cracks. In pursuit of continuous improvement in the quality of steel products, it is necessary to understand this phenomenon in its metallurgical dimension. This article aims to characterize this phenomenon using microscopy techniques, both optical and eletron scanning (SEM), evaluating the microstructure of the base material and of the centerline segregation zones and their correlation to chemical composition and microhardness.

Keywords

SEGREGAÇÃO CENTRAL; MICRODUREZA; ESTRUTURAS DE SOLIDIFICAÇÃO, Microestrutura

Slab Centerline Segregation; Microhardness; Solidification zones profile; microstructure