Title

ANÁLISE MICROESTRUTURAL E DE DUREZA EM AÇO 1080 TRATADO TERMICAMENTE POR TÊMPERA

MICROSTRUCTURAL AND HARDNESS ANALYSIS OF 1080 STEEL HEAT-TREATED BY TEMPERING.

Authorship

SOUSA, PALOMA SUELLEN LIMA DE; PORFÍRIO, DIOGO MONTEIRO; NASCIMENTO, DAMARES DA CRUZ BARBOSA; CANDIDO, VERONICA SCARPINI

SOUSA, PALOMA SUELLEN LIMA DE

I am this author

PORFÍRIO, DIOGO MONTEIRO

I am this author

NASCIMENTO, DAMARES DA CRUZ BARBOSA

I am this author

CANDIDO, VERONICA SCARPINI

I am this author

DOI

10.5151/2594-5327-41321

Downloads

Abstract

O AçO 1080, é UM MATERIAL CHAVE NA INFRAESTRUTURA, DEVIDO à SUA ELEVADA DUREZA E RESISTêNCIA AO DESGASTE. ESTE ESTUDO INVESTIGOU OS EFEITOS DO TRATAMENTO TéRMICO POR TêMPERA NO AçO CARBONO SAE 1080, PARA ISSO, AMOSTRAS DE AçO FORAM AQUECIDAS A 900°C POR 30 MINUTOS E RESFRIADAS RAPIDAMENTE EM áGUA. A METODOLOGIA INCLUIU A ANáLISE MICROESTRUTURAL POR MICROSCOPIA óPTICA E A AVALIAçãO DA DUREZA CONFORME A NORMA ABNT NBR ISO 6508-1, ALéM DA MEDIçãO DE TAMANHO DE GRãO COM O SOFTWARE IMAGEJ. INICIALMENTE, O AçO APRESENTAVA UMA ESTRUTURA COMPOSTA POR PERLITA E FERRITA, CONFERINDO-LHE UMA COMBINAçãO DE DUREZA E DUCTILIDADE. APóS A TêMPERA, A MICROESTRUTURA TRANSFORMOU-SE PREDOMINANTEMENTE EM MARTENSITA, RESULTANDO EM UMA DUREZA MéDIA DE 55 HRC, INDICANDO UMA TRANSFORMAçãO UNIFORME. A MAIORIA DOS GRãOS POSSUíA áREAS PEQUENAS, REFLETINDO UMA MICROESTRUTURA FINA E HOMOGêNEA APóS O TRATAMENTO. CONCLUIU-SE QUE A TêMPERA EM áGUA AUMENTA SIGNIFICATIVAMENTE A DUREZA DO AçO 1080, EMBORA A AUSêNCIA DE UM TRATAMENTO DE REVENIMENTO SUBSEQUENTE POSSA MANTER A FRAGILIDADE DEVIDO àS TENSõES RESIDUAIS ELEVADAS. ASSIM, O PROCESSO DE TêMPERA é EFICAZ PARA APLICAçõES ONDE A ALTA DUREZA é NECESSáRIA, MAS UM REVENIMENTO ADICIONAL é RECOMENDADO PARA MELHORAR A TENACIDADE E A RESISTêNCIA AO IMPACTO.

1080 STEEL IS A KEY MATERIAL IN INFRASTRUCTURE, DUE TO ITS HIGH HARDNESS AND WEAR RESISTANCE. THIS STUDY INVESTIGATED THE EFFECTS OF HEAT TREATMENT BY QUENCHING ON SAE 1080 CARBON STEEL. FOR THIS PURPOSE, STEEL SAMPLES WERE HEATED TO 900°C FOR 30 MINUTES AND QUICKLY COOLED IN WATER. THE METHODOLOGY INCLUDED MICROSTRUCTURAL ANALYSIS BY OPTICAL MICROSCOPY AND HARDNESS ASSESSMENT ACCORDING TO THE ABNT NBR ISO 6508-1 STANDARD, IN ADDITION TO GRAIN SIZE MEASUREMENT WITH IMAGEJ SOFTWARE. INITIALLY, STEEL HAD A STRUCTURE COMPOSED OF PEARLITE AND FERRITE, GIVING IT A COMBINATION OF HARDNESS AND DUCTILITY. AFTER QUENCHING, THE MICROSTRUCTURE TRANSFORMED PREDOMINANTLY INTO MARTENSITE, RESULTING IN AN AVERAGE HARDNESS OF 55 HRC, INDICATING A UNIFORM TRANSFORMATION. MOST GRAINS HAD SMALL AREAS, REFLECTING A FINE AND HOMOGENEOUS MICROSTRUCTURE AFTER TREATMENT. IT WAS CONCLUDED THAT WATER QUENCHING SIGNIFICANTLY INCREASES THE HARDNESS OF 1080 STEEL, ALTHOUGH THE ABSENCE OF A SUBSEQUENT TEMPERING TREATMENT MAY MAINTAIN BRITTLENESS DUE TO HIGH RESIDUAL STRESSES. THUS, THE QUENCHING PROCESS IS EFFECTIVE FOR APPLICATIONS WHERE HIGH HARDNESS IS REQUIRED, BUT ADDITIONAL TEMPERING IS RECOMMENDED TO IMPROVE TOUGHNESS AND IMPACT RESISTANCE.

Keywords

Aço 1080; Microestrutura; Dureza; Tratamento Térmico.

1080 steel; Microstructure; Toughness; Heat treatment.