Title

ANÁLISE QUANTITATIVA DOS INTERMETÁLICOS EM UMA LIGA MULTICOMPONENTE AL-CU-NI-TA SOLIDIFICADA EM UM DISPOSITIVO DIRECIONAL ASCENDENTE

QUANTITATIVE ANALYSIS OF INTERMETALLICS IN A MULTICOMPONENT ALLOY AL-CU-NI-TA SOLIDIFIED IN AN UPWARD DIRECTIONAL DEVICE

Authorship

JESUS, WELLINGTON BRUNO SILVA DE

JESUS, WELLINGTON BRUNO SILVA DE

I am this author

DOI

10.5151/Fault-41192

Downloads

Abstract

A CRESCENTE DEMANDA DA INDúSTRIA MODERNA POR MATERIAIS COM PROPRIEDADES ELEVADAS E ESPECíFICAS REQUER UM CONHECIMENTO APROFUNDADO DO PROCESSO DE SOLIDIFICAçãO DE METAIS E LIGAS METáLICAS. ESTE TRABALHO TEVE COMO FINALIDADE A QUANTIFICAçãO DOS INTERMETáLICOS FORMADOS DURANTE O PROCESSO DE SOLIDIFICAçãO DA LIGA MULTICOMPONENTE AL-33%CU-1%NI-1,2%TA EM UM DISPOSITIVO DIRECIONAL ASCENDENTE, ENALTECENDO A NOVIDADE DESTA LIGA. A CARACTERIZAçãO FOI REALIZADA EM UMA AMOSTRA ATRAVéS DE METALOGRAFIA, SEGUIDA DE ANáLISE POR MICROSCOPIA ELETRôNICA DE VARREDURA (MEV). APóS A OBTENçãO DAS MICROGRAFIAS EM REGIõES REPRESENTATIVAS ONDE OCORREU A IDENTIFICAçãO DOS INTERMETáLICOS, FORAM MEDIDOS OS ESPAçAMENTOS LAMELARES DO AL2CU (λL1), áREA DO INTERMETáLICO NO FORMATO DE ESTRELA E ESPAçAMENTO LAMELAR DO EUTéTICO AO REDOR DA ESTRELA (λL2). OS RESULTADOS TAMBéM FORAM COMPARADOS COM ESTUDOS REALIZADOS ANTERIORMENTE, E MOSTRARAM A GRANDE INFLUêNCIA DOS PARâMETROS TéRMICOS NAS REAçõES DE FORMAçãO DOS INTERMETáLICOS AO LONGO DO LINGOTE.

MODERN INDUSTRY'S INCREASING DEMAND FOR MATERIALS WITH HIGH AND SPECIFIC PROPERTIES REQUIRES AN IN-DEPTH KNOWLEDGE OF THE SOLIDIFICATION PROCESS OF METALS AND METAL ALLOYS. THIS WORK AIMED TO QUANTIFY THE INTERMETALLICS FORMED DURING THE SOLIDIFICATION PROCESS OF THE MULTICOMPONENT ALLOY AL-33%-1%NI-1.2%TA IN AN UPWARD DIRECTIONAL DEVICE, ENHANCING THE NOVELTY OF THIS ALLOY. CHARACTERIZATION WAS PERFORMED ON A SAMPLE BY METALLOGRAPHY, FOLLOWED BY SCANNING ELECTRON MICROSCOPY (SEM) ANALYSIS. AFTER OBTAINING THE MICROGRAPHS IN REPRESENTATIVE REGIONS WHERE THE INTERMETALLICS WERE IDENTIFIED, THE LAMELLAR SPACING OF THE AL2CU (λL1), THE AREA OF THE INTERMETALLIC IN THE SHAPE OF A STAR, AND THE LAMELLAR SPACING OF THE EUTECTIC AROUND THE STAR (λL2) WERE MEASURED. THE RESULTS WERE ALSO COMPARED WITH PREVIOUS STUDIES, AND SHOWED THE SIGNIFICANT INFLUENCE OF THERMAL PARAMETERS ON THE FORMATION REACTIONS OF INTERMETALLICS ALONG THE INGOT.

Keywords

Ligas de alumínio; Solidificação; Intermetálicos

Aluminum alloys; Solidification; Intermetallics.