ANÁLISE TERMOGRAVIMÉTRICA DE UM COMPÓSITO TRIPLA CAMADA REFORÇADO COM FIBRA DE VIDRO E APLICADO EM TUBULAÇÕES DE PETRÓLEO

THERMOGRAVIMETRIC ANALYSIS OF A THREE-LAYERED POLYMERIC COMPOSITE REINFORCED WITH FIBERGLASS AND APPLIED IN OIL PIPES

Authorship

Gomes, Italo Martins

DOI

10.5151/2594-5327-34011

Downloads

heading.download_article_detail 24 Downloads

Abstract

A INDÚSTRIA DO PETRÓLEO E GÁS TEM CONSTANTEMENTE SE DEPARADO COM PROBLEMAS DE CORROSÃO EM EQUIPAMENTOS, DEVIDO À CARATERÍSTICA QUÍMICA DO PETRÓLEO, DO GÁS E DOS CONTAMINANTES NOS RESERVATÓRIOS. EM 2010, FOI DESENVOLVIDO UM COMPÓSITO POLIMÉRICO TRIPLA CAMADA, REFORÇADO COM FIBRA DE VIDRO, PARA TUBULAÇÕES DE PRODUÇÃO TERRESTRES DE PETRÓLEO, COMO ALTERNATIVA AO AÇO API 5L GRAU B, COMUMENTE UTILIZADO E MAIS SUSCETÍVEL À CORROSÃO. NO PRESENTE TRABALHO, COLETOU-SE AMOSTRAS DE TUBOS DESSE COMPÓSITO EM DOIS POÇOS DE PETRÓLEO QUE OPERAM COM ESSE MATERIAL HÁ ALGUNS ANOS. AS CAMADAS INTERNAS E EXTERNAS (EM CONTATO COM FLUIDO E SOLO, RESPECTIVAMENTE) DAS AMOSTRAS DOS POÇOS FORAM ANALISADAS POR TERMOGRAVIMETRIA (TGA) E TERMOGRAVIMETRIA DERIVADA (DTGA) E COMPARADAS COM UMA AMOSTRA CONTROLE NOVA, A FIM DE AVALIAR SE HOUVE ALGUM EVENTO INDESEJÁVEL OU DEGRADAÇÃO DAS CAMADAS E CONHECER OS LIMITES DE TEMPERATURA DESSE NOVO MATERIAL. OS RESULTADOS MOSTRARAM QUE NÃO HOUVE ALTERAÇÃO SIGNIFICATIVA NAS AMOSTRAS DOS POÇOS (SE COMPARADO A AMOSTRA CONTROLE), POIS OS MESMOS EVENTOS OCORRERAM EM TEMPERATURAS SIMILARES. TAMBÉM FOI VISTO QUE O MATERIAL ESTÁ APTO PARA TRABALHAR NA TEMPERATURA ESPECIFICADA DO SEU DESENVOLVIMENTO, POIS OS EVENTOS OCORRERAM ACIMA DE 200°C.

 

THE OIL AND GAS INDUSTRY HAS CONSTANTLY FACED PROBLEMS WITH EQUIPMENT CORROSION, DUE TO THE CHEMICAL CHARACTERISTICS OF OIL, GAS AND CONTAMINANTS IN RESERVOIRS. IN 2010, A POLYMERIC COMPOSITE, REINFORCED WITH FIBERGLASS, WAS DEVELOPED FOR OIL PIPES, AS AN ALTERNATIVE TO API 5L GRADE B STEEL, COMMONLY USED AND MORE SUSCEPTIBLE TO CORROSION. IN THE PRESENT WORK, SAMPLES OF TUBES OF THIS COMPOSITE WERE COLLECTED IN TWO OIL WELLS THAT HAVE BEEN OPERATING WITH THIS MATERIAL FOR SOME YEARS. THE INTERNAL AND EXTERNAL LAYERS (IN CONTACT WITH FLUID AND SOIL, RESPECTIVELY) OF THE WELL SAMPLES WERE ANALYZED BY THERMOGRAVIMETRY (TGA) AND DERIVED THERMOGRAVIMETRY (DTGA) AND COMPARED WITH A NEW SAMPLE, TO ASSESS WHETHER THERE WERE ANY UNDESIRABLE EVENTS OR DEGRADATION OF THE LAYERS AND KNOW THE TEMPERATURE LIMITS OF THIS NEW MATERIAL. THE RESULTS SHOWED THAT THERE WAS NO SIGNIFICANT CHANGE IN THE SAMPLES FROM THE WELLS (IF COMPARED TO THE CONTROL SAMPLE), AS THE SAME EVENTS OCCURRED AT SIMILAR TEMPERATURES. IT WAS ALSO SEEN THAT THE MATERIAL IS ABLE TO WORK AT THE SPECIFIED TEMPERATURE OF ITS DEVELOPMENT, AS THE EVENTS OCCURRED ABOVE 200°C..

Keywords

Análise térmica; termogravimetria; compósito; tubulação de petróleo.

thermogravimetry; composite; oil pipe; fiberglass; epoxy.